Vinyl-cis-polybutadiene rubber and butadiene rubber composition using the same
View Patent ↗A vinyl•cis-polybutadiene rubber is provided containing 1,2-polybutadiene and a polymer substance of a melting point lower than that of the 1,2-polybutadiene and with at least one unsaturated double bond per repeating unit, where the 1,2-polybutadiene and the polymer substance are dispersed at physically and/or chemically adsorbed states in the cis-polybutadiene rubber as the matrix component of the vinyl•cis-polybutadiene rubber, and a method for producing the same, to provide a vulcanized product exerting a small die swell ratio and excellent extrusion processability and operability, as well as very great characteristics demanded for the side tread of tire and the like.
1. A method for producing vinyl•cis-polybutadiene rubber by a step of cis-1,4 polymerization of 1,3-butadiene using a cis-1,4 polymerization catalyst in a hydrocarbon-series solvent to obtain a first polymerization mixture, a step of 1,2 polymerization of 1,3-butadiene in the concurrent presence of a 1,2 polymerization catalyst in the first polymerization mixture to generate a second polymerization mixture including 1,2-polybutadiene having a melting point of 170° C. or more, and a step of separation and recovery of vinyl•cis-polybutadiene rubber generated from the second polymerization mixture, the method further including a step of adding a polymer substance with at least one unsaturated double bond per repeating unit to the production system of vinyl•cis-polybutadiene rubber, wherein the polymer substance comprises at least one selected from the group consisting of polyisoprene, crystallizable polybutadiene having a melting point less than 170° C., liquid polybutadiene, a polymeric compound containing an ether group, an epoxy group, a carboxyl group, an ester group, a hydroxyl group, or a carbonyl group, and derivatives of the polymer substance thereof.
2. The method for producing vinyl•cis-polybutadiene rubber according to claim 1 , where the polymer substance comprises at least one selected from the group consisting of polyisoprene, crystallizable polybutadiene having a melting point of 0° C. to 150° C., liquid polybutadiene, and derivatives thereof.
3. The method for producing vinyl•cis-polybutadiene rubber according to claim 1 , where the amount of the polymer substance to be added to the production system is within a range of 0.01 to 50% by mass to the vinyl•cis-polybutadiene rubber to be obtained.
4. The method for producing vinyl•cis-polybutadiene rubber according to claim 1 , wherein the step of adding the polymer substance to the production system comprises adding the polymer substance appropriate time point from the step of the cis-1,4 polymerization to the step of the separation and recovery of the vinyl•cis-polybutadiene rubber generated from the second polymerization mixture obtained after the completion of the 1,2 polymerization.
5. The method for producing vinyl•cis-polybutadiene rubber according to claim 1 , where the hydrocarbon-series solvent is a hydrocarbon-series solvent with a solubility parameter of 9.0 or less.
6. A butadiene rubber composition prepared by compounding the vinyl•cis-polybutadiene rubber obtained by a production method according to claims 1 at 10 to 300 parts by mass per 100 parts by mass of a rubber selected from natural rubber, polyisoprene rubber, styrene-butadiene copolymer rubber or a blend rubber of at least two types thereof.
7. A butadiene rubber composition for tire, comprising the vinyl•cis-polybutadiene rubber obtained by a production method according to claim 1 .
8. A butadiene rubber composition for tire, where the vinyl•cis-polybutadiene rubber obtained by a production method according to claim 1 is used at 10 to 300 parts by weight per 100 parts by weight of a rubber selected from natural rubber, polyisoprene rubber, styrene-butadiene copolymer, rubber, or a blend rubber of at least two types thereof.