Friction surface for wet clutch
View Patent ↗A friction lining made of a fibrous mixture with fillers and resin for a wet clutch. In order to design the friction lining able to withstand the higher torque to be transmitted, it is proposed to admix further filler with a Mohs hardness greater or equal to 9.0 and smaller or equal to 9.5 in addition to the ingredients of aramid fibers, cellulose fibers, phenol resin and amorphous silicon dioxide and first filler.
1. A friction lining containing, based on 100% percentage by weight, the following ranges:
30% to 60% cellulose fibers,
10% to 20% aramid fibers,
15% to 45% an amorphous silicon dioxide, and
1% to 10% a silicon carbide having a Mohs hardness greater than or equal to 9.0 and smaller than or equal to 9.5,
with a further 15% to 44% phenol resin add-on.
2. The friction lining as recited in claim 1 wherein the amorphous silicon dioxide is a diatomaceous earth.
3. The friction lining as recited in claim 1 wherein the friction lining contains the silicon carbide in a proportion smaller than 10% in percentage by weight.
4. The friction lining as recited in claim 3 wherein the friction lining contains silicon carbide in a proportion smaller than 6% in percentage by weight.
5. The friction lining as recited in claim 1 wherein the aramid fibers have a CSF-value between 550 and 650.
6. The friction lining as recited in claim 1 wherein the friction lining features the following composition in percentage by weight:
45% cellulose fibers,
15% aramid fibers,
35% amorphous silicon dioxide, and
5% silicon carbide,
with a further 33% phenol resin add-on.
7. The friction lining as recited in claim 6 wherein the amorphous silicon dioxide is a diatomaceous earth.
8. The friction lining as recited in claim 1 wherein the friction lining is for a wet clutch.