View Patent ↗Crosslinked pressure-sensitive adhesive comprising at least one base polymer component obtainable by free-radical copolymerization of the following monomers: a) linear acrylic esters having 2 to 10 C atoms in the alkyl radical, b) branched, non-cyclic acrylic esters having a glass transition temperature T g (based on the DSC measurement to DIN 53765) of not more than −20° C., c) 8% to 15% by weight of acrylic acid, d) optionally up to 10% by weight of further copolymerizable monomers, characterized in that the ratio of the linear acrylic esters to the branched acrylic esters is in the range from 1:6 to 10:1 mass fractions.
1. Crosslinked pressure-sensitive adhesive comprising at least one polymer component obtained by free-radical copolymerization of the following monomers exclusively:
a) linear acrylic esters having 2 to 10 C atoms in the alkyl radical,
b) branched, non-cyclic acrylic esters having a glass transition temperature T g , of not more than −20° C., and
c) acrylic acid, in an amount of at least 11% up to 13% by weight, based on the total weight of monomers,
wherein the mass ratio of the linear acrylic esters to the branched acrylic esters is in the range from 1:6 to 10:1.
2. Pressure-sensitive adhesive according to claim 1 , said at least one polymer component makes up at least 90% by weight of the pressure-sensitive adhesive.
3. Pressure-sensitive adhesive according to claim 1 , wherein said amount of acrylic acid is up to 12.5% by weight, based on the total weight of monomers copolymerized.
4. Pressure-sensitive adhesive according to claim 1 , wherein the mass ratio of the linear acrylic esters to the branched acrylic esters is in the range of 1:5 to 9:1.
5. Pressure-sensitive adhesive according to claim 1 , wherein the mass ratio of the linear acrylic esters to the branched acrylic esters is from 1.5:1 to 3.5:1.
6. Pressure-sensitive adhesives according to claim 1 , wherein said liner acrylic ester is butyl acrylate and said branched non-cyclic acrylic ester is 2-ethylhexyl acrylate.
7. A method for bonding flexible printing plates to curved surfaces which comprises bonding said flexible printing plates to said curved surfaces with the pressure-sensitive adhesive of claim 1 .
8. Method of claim 7 , wherein said pressure-sensitive adhesive has a solvent resistance that corresponds to edge lifting of less than 10 mm under the influence of solvent.
9. The pressure-sensitive adhesive of claim 2 , wherein said at least one polymer component makes up at least 95% by weight of the pressure-sensitive adhesive.
10. The pressure-sensitive adhesive of claim 9 , wherein said at least one polymer component makes up at least 98% by weight of the pressure-sensitive adhesive.
11. Pressure-sensitive adhesive according to claim 3 , wherein said amount of acrylic acid is from 11% to 12% by weight, based on the total weight of monomers copolymerized.
12. Pressure-sensitive adhesive according to claim 1 , wherein said amount of acrylic acid is 13% by weight, based on the total weight of monomers copolymerized.
13. The pressure sensitive adhesive of claim 4 , wherein said mass ratio of the linear acrylic esters to the branched acrylic esters is from 1:2 to 4:1.
14. The pressure-sensitive adhesive of claim 5 , wherein said mass ratio of the linear acrylic esters to the branched acrylic esters is from 2:1 to 3:1.
15. The method of claim 8 , wherein said edge lifting is less than 5 mm.
16. The crosslinked pressure-sensitive adhesive of claim 1 , wherein said monomers further comprise up to 10% by weight of additional copolymerizable monomers.