Manufacturing method of laminated metal plate and laminated metal plate manufactured by the method
In the manufacturing method of the laminated metal plate, a fluorine resin film is used as a plastic film. Prior to a flame treatment, a joint surface of the metal plate is heated with a direct flame of 900° C. to 1200° C. for 1 to 5 seconds so that the joint surface is preheated to 40° C. to 70° C. After that, the joint surface of the metal plate is heated to 250° C. to 450° C. by the follow-on flame treatment.
1. A laminated metal plate in which a laminated metal plate in which a joint surface of a metal plate with a thickness of 0.1 mm to 1.00 mm and without a pretreatment like degreasing, washing, a chemical conversion treatment or a primer treatment, is flamed with a direct fire of 1400° C. to 1600° C. to directly join a plastic film under pressure, wherein said plate is made by a method comprising the steps of:
using a fluorine resin film as the plastic film,
flaming the joint surface of the metal plate with a direct fire of 900° C. to 1200° C. for 1 to 5 seconds prior to the above-mentioned flame treatment, so that the temperature of the joint surface may be preheated to 40° C. to 70° C., and then
heating the joint surface of the metal plate by the follow-on flame treatment so that the temperature of the joint surface is heated to 250° C. to 450° C.
2. The laminated metal plate as claimed in claim 1 , wherein the fluorine resin film is composed of ethylene-tetrafluoroethylene-based copolymer.