Graphite particles and lithium secondary battery using the same as negative electrode
View Patent ↗A graphite particle obtained by assembling or binding together a plurality of flat-shaped particles so that the planes of orientation are not parallel to one another, or a graphite particle in which aspect ratio is 5 or less or specific surface area is 8 m 2 /g or less or the size of crystallite in the direction of c-axis of the crystal is 500 Å or more and the size of crystallite in the direction of plane is 1,000 Å or less as measured by X ray broad angle diffraction, or a graphite particle in which pore volume of the pores having a size falling in a range of 10 2 to 10 6 Å is 0.4 to 2.0 cc/g per weight of graphite particle or pore volume of the pores having a size falling in a range of 1×10 2 to 2×10 4 Å is 0.08 to 0.4 cc/g per weight of graphite particle is suitable for production of negative electrode of lithium secondary battery, and a lithium secondary battery obtained therefrom is excellent in rapid charge-discharge characteristics, cycle characteristics, etc.
1. A negative electrode for a lithium secondary battery obtained by coating a mixture of graphite particles and organic binder on a current collector, wherein the density of the mixture of graphite particles and organic binder is 1.5 to 1.9 g/cm 3 as measured after integration with pressing, and wherein pore volume of the pores having a size falling in the range of 10 2 to 10 6 Å of the graphite particles is 0.4 to 2.0 cc/g per weight of graphite particles.
2. A negative electrode for lithium secondary battery according to claim 1 , wherein the content of said organic binder is 11 to 20% by weight based on the mixture of graphite particles and organic binder.
3. A negative electrode for lithium secondary battery according to claim 1 , wherein the content of said organic binder is 3 to 20% by weight based on the mixture of graphite particles and organic binder.
4. A negative electrode for lithium secondary battery according to claim 1 , wherein aspect ratio of said graphite particles is 5 or less.
5. A negative electrode for lithium secondary battery according to claim 1 , wherein specific surface area of said graphite particles is 8 m 2 /g or less.
6. A negative electrode for lithium secondary battery according to claim 1 , wherein the size of crystallite in the direction of c-axis (direction of thickness) of crystal of the graphite particles is 500 Å or more as measured by means of X-ray broad angle diffraction of the graphite particles.
7. A negative electrode for lithium secondary battery according to claim 1 , wherein said graphite particles are obtained by assembling or binding together a plurality of flat-shaped particles so that the planes of orientation are not parallel to one another.