Catalyst life improvement for the vapor phase manufacture of 1-chloro-3,3,3-trifluoropropene
View Patent ↗This invention achieves a catalyst life improvement for the catalyzed vapor phase reaction of 1,1,1,3,3-pentachloropropane with hydrogen fluoride to form 1-chloro-3,3,3-trifluoropropene by introducing an oxygen co-feed into the fluorination reactor. By introduction of an oxygen co-feed to the reactor feed, the catalyst life was extended a minimum of two-fold (2×).
1. A method of extending the lifetime of a catalyst used in the vapor phase catalytic fluorination reaction of the raw materials 1,1,1,3,3-pentachloro-propane (HCC-240fa) and hydrogen fluoride (HF) to produce 1-chloro-3,3,3-trifluoropropene, comprising the step of introducing an oxygen co-feed into the fluorination reaction, thereby extending the catalyst life during the fluorination reaction.
2. The method of claim 1 , wherein the catalyst life is extended by at least two-fold.
3. The method of claim 1 , wherein the oxygen is introduced together with the feeds of the raw materials 1,1,1,3,3-pentachloropropane and hydrogen fluoride.
4. The method of claim 1 , wherein the oxygen is introduced after the raw materials 1,1,1,3,3-pentachloropropane and hydrogen fluoride have been vaporized.
5. The method of claim 1 , wherein the oxygen is introduced before the raw materials 1,1,1,3,3-pentachloropropane and hydrogen fluoride have been vaporized.
6. The method of claim 1 , wherein the source of oxygen is selected from the group consisting of oxygen gas, dry air, and oxygen gas diluted with an inert gas.
7. The method of claim 1 , wherein the molar ratio of oxygen to 1,1,1,3,3-pentachloropropane is between 0.005 to 1 and 0.1 to 1.
8. The method of claim 1 , wherein the molar ratio of oxygen to 1,1,1,3,3-pentachloropropane is between 0.01 to 1 and 0.07 to 1.
9. The method of claim 1 , wherein the molar ratio of oxygen to 1,1,1,3,3-pentachloropropane is between 0.02 to 1 and 0.05 to 1.
10. The method of claim 1 , wherein the catalyst is selected from the group consisting of chromium, aluminum, cobalt, manganese, nickel and iron oxides, hydroxides, halides, oxyhalides, inorganic salts thereof and their mixtures.
11. The method of claim 1 , wherein the catalyst is selected from the group consisting of Cr 2 O 3 , Cr 2 O 3 /Al 2 O 3 , Cr 2 O 3 /AlF 3 , Cr 2 O 3 /carbon, CoCl 2 /Cr 2 O 3 /Al 2 O 3 , NiCl 2 /Cr 2 O 3 /Al 2 O 3 , CoCl 2 /AlF 3 , NiCl 2 /AlF 3 and mixtures thereof.
12. The method of claim 1 , wherein the catalyst comprises one or more chromium (III) oxides.
13. The method of claim 12 , wherein the catalyst comprises crystalline chromium oxide.
14. The method of claim 12 , wherein the catalyst comprises amorphous chromium oxide.
15. The method of claim 14 , wherein the catalyst is at least partially fluorinated.
16. The method of claim 1 , wherein the catalyst is selected from the group consisting of FeCl 3 , SnCl 4 , TaCl 5 , SbCl 3 , AlCl 3 , and AlF 3 , supported on carbon.
17. The method of claim 1 , wherein the catalyst is selected from the group consisting of FeCl 3 , SnCl 4 , TaCl 5 , SbCl 3 , A 1 Cl 3 , and AlF 3 , supported on alumina.
18. The method of claim 1 , wherein the catalyst is selected from the group consisting of FeCl 3 , SnCl 4 , TaCl 5 , SbCl 3 , AlCl 3 , and AlF 3 , supported on fluorinated alumina.
19. A method of extending the lifetime of a catalyst used in the vapor phase catalytic fluorination reaction of the raw materials 1,1,1,3,3-pentachloro-propane and hydrogen fluoride to produce 1-chloro-3,3,3-trifluoropropene, comprising the steps of:
(a) monitoring the exotherm of the active catalyst relative to the external reactor heater, and
(b) adding an oxygen co-feed into the fluorination reaction to retard the deactivation of the catalyst during the fluorination reaction.
20. The method of claim 19 , wherein the oxygen co-feed retards the deactivation of the catalyst compared to when no oxygen co-feed is employed.