Process for making an embossed web
A process for making an embossed web. A precursor web is provided between a forming structure and a static pressure plenum. The forming structure has a plurality of discrete apertures or depressions. Pressure is provided by the static pressure plenum against the precursor web and the forming structure to force the precursor web into the apertures or depressions of forming structure to form the embossed web. The resulting embossed web has a plurality of discrete extended elements.
1. A process for making an embossed film web, comprising:
feeding a precursor film web between a static gas pressure plenum and a forming structure comprising a plurality of discrete apertures, discrete depressions, or combinations thereof, the apertures or depressions having a depth of at least substantially equal to a thickness of the precursor web, and wherein the static gas pressure plenum creates static pressure conditions;
applying static pressure from the static gas pressure plenum against the precursor web opposite the forming structure creating a pressure differential across the precursor web sufficient to force the precursor web into the apertures or depressions of the forming structure, thereby forming the embossed web comprising a plurality of discrete extended elements having open proximal ends; and
applying pressure from a second pressure source against the precursor web sufficient to force portions of the precursor web into void volumes defined by the apertures or depressions, wherein the pressure from the second pressure source is applied sequentially before or after the static pressure is applied against the precursor web from the static gas pressure plenum.
2. The process of claim 1 , comprising feeding the precursor web between the static gas pressure plenum and the forming structure at a rate of at least about 1 meter per second.
3. The process of claim 1 , comprising applying pressure for a dwell time of about 1 millisecond to about 5 seconds.
4. The process of claim 1 , wherein the temperature of the precursor web during the process is less than the melting point of the precursor web.
5. The process of claim 4 , wherein the temperature of the precursor web at least about 10° C. below the melting point of the precursor web.
6. The process of claim 1 , wherein the temperature of the precursor web during the process is about 20° C. to about 110° C.
7. The process of claim 1 , wherein the gas comprises at least one gas selected from the group consisting of nitrogen, carbon dioxide, and mixtures thereof.
8. The process of claim 1 , wherein the gas comprises air.
9. The process of claim 1 , wherein the apertures or depressions have a depth of at least three times the thickness of the precursor web.
10. The process of claim 1 , wherein the apertures or depressions of the forming structure have an average edge-to-edge spacing of about 30 microns to about 800 microns.
11. The process of claim 1 , wherein the apertures or depressions of the forming structure having an average width of about 10 microns to about 5 mm.
12. The process of claim 1 , wherein the apertures or depressions have a depth of about 25 microns to about 5000 microns.
13. The process of claim 1 , wherein the extended elements of the embossed web have open distal ends.
14. The process of claim 1 , wherein the extended elements of the embossed web have closed distal ends.
15. The process of claim 1 , wherein the extended elements of the embossed web have an aspect ratio of at least about 0.2.
16. The process of claim 1 , wherein the applied pressure is about 0.1 MPa to about 25 MPa.
17. The process of claim 16 , wherein the applied pressure is about 0.5 MPa to about 5 MPa.
18. The process of claim 1 , wherein the extended elements are thinned relative to the thickness of the precursor web.
19. The process of claim 1 , wherein the applied pressure is sufficient to stretch the precursor web beyond the yield point of the precursor web.
20. The process of claim 1 , wherein the precursor web is selected from the group consisting of polyethylene, polypropylene, and blends thereof.
21. The process of claim 1 , wherein pressure is applied from the second pressure source before pressure is applied from the static gas pressure plenum.
22. The process of claim 1 , wherein pressure is applied from the second pressure source after pressure is applied from the static gas pressure plenum.
23. The process of claim 1 , wherein the second pressure source is selected from the group consisting of a static liquid pressure plenum, a static gas pressure plenum, a velocity gas pressure source, a velocity liquid pressure source, and a compliant substrate.