Method of making an embossed metal gasket

1. A method of making an embossed metal gasket, comprising the steps of:

forming an annealed sheet of an iron-nickel-chromium alloy;

cold rolling the annealed sheet without shaping to produce a cold-rolled, work hardened microstructure of the sheet; and

forming a gasket from said sheet including cold forming a least one embossed sealing bead which imparts further work hardening in the area of the at least one sealing bead wherein the at least one sealing bead is sealably operable with substantially full functional recovery in a fully-clamped, sealed joint at a temperature of greater than 1100° F. and up to 1200° F. without post-embossment heat treating of the sealing bead to provide the finished sealing bead with at least a portion of the work hardened microstructure as cold-rolled and embossed.

2. The method of claim 1 , wherein the percentage of cold reduction from cold rolling ranges from 10-70%.

3. The method of claim 2 , wherein the percentage of cold reduction ranges from 30-40%.

4. The method of claim 1 , wherein the step of deforming produces a degree of deformation sufficient to provide said deformed sheet with a tensile elongation in a rolling direction of at least 5%.

5. The method of claim 4 , wherein said step of deforming produces a degree of deformation sufficient to provide said deformed sheet with a tensile elongation in a rolling direction of about 5-10%.

6. The method of claim 1 , further comprising a step of:

providing a precipitation hardening heat treatment after the cold rolling step and before the cold forming of the at least one bead, wherein the deformed microstructure further comprises a deformed and precipitation hardened microstructure, wherein the deformed and precipitation hardened microstructure has a hardness which is greater than a hardness of the deformed microstructure.

7. The method of claim 6 , wherein the precipitation hardening heat treatment is performed at a temperature of between about 1200-1350° F. for about 8-15 hours.

8. The method of claim 1 , further comprising the step of:

coating the gasket with a heat resistant coating.

9. The method of claim 8 , wherein the heat resistant coating comprises:

chemically exfoliated vermiculite wherein at least 90 weight percent of the vermiculite has a thickness of less than or equal to 30 microns and no dimension is greater than 1 millimeter;

a high temperature organic resin that is heat resistant to at least 300 degrees Celsius;

a supplementary inorganic resin; and

a flaky filler.