Paper substrate having enhanced print density
The present invention relates to a sizing composition that, when applied to paper substrate, creates a substrate, preferably suitable for inkjet printing, having increased print density, print sharpness, low HST, and/or image dry time, the substrate preferably having high brightness and reduced color-to-color bleed as well. In addition, the present invention relates to a method of reducing the HST of a paper substrate by applying the sizing composition to at least one surface thereof. Further, the application relates to methods of making and using the sizing composition, as well as methods of making and using the paper containing the sizing composition.
1. A sizing composition, comprising
at least one pigment;
at least one polyvinyl alcohol binder and at least one starch binder at a starch/polyvinyl alcohol weight ratio of from 10/1 to 1/5;
at least one nitrogen containing organic species;
at least one inorganic salt; and
10 to 75 wt % of an optical brightening agent based on the total weight of the solids in the composition.
2. The sizing composition according to claim 1 , wherein the polyvinyl alcohol and starch are present at a starch/polyvinyl alcohol weight ratio of from 8/1 to 1/1.
3. The sizing composition according to claim 2 , wherein the total binder is present at an amount ranging at least 20 wt %, based upon the total weight of the solids in of the composition.
4. The sizing composition according to claim 2 , further comprising from 20 to 40 wt % based on the total weight of the solids in the composition of an optical brightening agent.
5. The sizing composition according to claim 1 , wherein the optical brightening agent is cationic.
6. The sizing composition according to claim 1 , comprising
at least one pigment at an amount of at least 30 wt % based upon the total weight of the solids in of the composition;
at least two binders at an amount of at least 20 wt % based upon the total weight of the solids in of the composition, wherein at least one binder is polyvinyl alcohol and wherein at least one binder is starch at a starch/polyvinyl alcohol weight ration of from 10/1 to 1/5;
at least one nitrogen containing organic species at an amount ranging from 1 to 20 wt % based upon the total weight of the solids in of the composition; and
at least one inorganic salt at an amount ranging from 0.5 to 5 wt % based upon the total weight of the solids in of the composition.
7. The sizing composition according to claim 6 , comprising starch and polyvinyl alcohol at a weight ratio of from 8/1 to 1/1 starch/polyvinyl alcohol; and an optical brightener.
8. A paper substrate, comprising the sizing composition according to claim 1 .
9. The paper substrate according to claim 8 , wherein the substrate has a print density of at least 1.0 and an HST of not more than 10 seconds.
10. The paper substrate according to claim 9 , wherein the substrate has a waterfastness of at least 95%.
11. A paper substrate comprising the sizing composition according to claim 2 .
12. The paper substrate according to claim 11 , wherein the substrate has a print density of at least 1.0 and an HST of not more than 10 seconds.
13. The paper substrate according to claim 12 , wherein the substrate has a waterfastness of at least 95%.
14. A paper substrate comprising the sizing composition according to claim 6 .
15. The paper substrate according to claim 14 , wherein the substrate has a print density of at least 1.0 and an HST of not more than 10 seconds.
16. The paper substrate according to claim 15 , wherein the substrate has a waterfastness of at least 95%.
17. A paper substrate, comprising the sizing composition according to claim 7 and having a print density of at least 1.0; an HST of not more than 10 seconds; and a waterfastness of at least 95%.