Method of electropolishing medical implants
View Patent ↗An electropolishing apparatus and method are provided for polishing stents and other medical implants. The apparatus includes a motor that rotates a roller. The roller continuously rotates the medical implant to be electropolished. One of the advantages of the apparatus and method is that marks generated around the electrical contact between the anode and the medical implant are minimized. In addition, the medical implant is polished more evenly than conventional electropolishing systems.
1. A method of electro-polishing a medical implant, comprising:
establishing a predetermined cumulative current flow to be used to control an amount of time said medical implant is electro-polished;
immersing said medical implant, an anode and a cathode in an electrolytic bath;
contacting a surface of said medical implant with said anode, thereby forming an electrical contact;
continuously moving said electrical contact between said medical implant and said anode in said electrolytic bath, thereby continuously changing said electrical contact;
applying a voltage across said anode and said cathode,
measuring an actual cumulative current flow between said anode and said cathode;
electro-polishing said medical implant until said actual cumulative current flow reaches said predetermined cumulative current flow; and
wherein said medical implant is electro-polished while being immersed in said electrolytic bath, the generation of marks on said medical implant at said electrical contact thereby being minimized.
2. The method according to claim 1 , wherein said medical implant is rotated between about 5 revolutions per minute and 60 revolutions per minute.
3. The method according to claim 2 , wherein said medical implant is rotated about 35 revolutions per minute.
4. The method according to claim 1 , wherein said anode contacts an inner surface of said medical implant.
5. The method according to claim 1 , wherein said anode extends along an entire length of said medical implant.
6. The method according to claim 1 , wherein said medical implant is continuously rotated.
7. The method according to claim 1 , wherein said anode is a wire extending longitudinally through a cylindrical cavity of said medical implant, said anode contacting an inner surface of said medical implant along a side surface of said wire.
8. The method according to claim 7 , wherein said anode has a diameter 75% or less than an inner diameter of said cylindrical cavity.
9. The method according to claim 1 , wherein said anode is made from platinum and said cathode is made from a same material as said medical implant.
10. The method according to claim 1 , wherein said anode is oriented at an angle with respect to said cathode.
11. The method according to claim 1 , wherein said anode is oriented at an angle between a horizontal orientation and a vertical orientation; and said anode is attached to a swing arm, said swing arm adapted to lift said anode and medical implant out of said electrolytic bath.
12. The method according to claim 1 , wherein said anode contacts an inner surface of said medical implant and said medical implant is continuously rotated.
13. The method according to claim 12 , wherein said anode is a wire extending longitudinally through a cylindrical cavity of said medical implant, said anode contacting an inner surface of said medical implant along a side surface of said wire, and said medical implant is rotated between about 5 revolutions per minute and 60 revolutions per minute.
14. The method according to claim 13 , wherein said anode has a diameter 75% or less than an inner diameter of said cylindrical cavity and said anode is made from platinum and said cathode is made from a same material as said medical implant.
15. The method according to claim 14 , wherein said anode is oriented at an angle with respect to said cathode and said anode extends along an entire length of said medical implant.
16. The method according to claim 1 , wherein medical implant is continuously rotated and said medical implant is rotated between about 5 revolutions per minute and 60 revolutions per minute.
17. The method according to claim 16 , wherein said anode is made from platinum and said cathode is made from a same material as said medical implant.
18. The method according to claim 17 , wherein said anode is oriented at an angle with respect to said cathode.
19. The method according to claim 18 , wherein said medical implant is rotated about 35 revolutions per minute.