Anti-reflective film and production method thereof, and stamper for producing anti-reflective film and production method thereof
View Patent ↗In this method for producing an anti-reflective film, pores are formed on a surface of a polymer molding material to continuously change a refractive index and then reduce reflectance, in which anodic oxidized porous alumina, in which pores having a tapered shape and whose pore diameter continuously changes, are formed by repeating anodic oxidation at about the same formation voltage and pore diameter enlargement treatment, is used as a mold, or a stamper, which is produced by using the anodic oxidized porous aluminum as a mold, is used as a mold.
1. A mold composed of anodic oxidized porous alumina, comprising: a plurality of pores having a diameter decreases stepwise along a depth direction thereof, and formed by repeating anodic oxidation and pore diameter enlargement treatment.
2. The mold composed of anodic oxidized porous alumina according to claim 1 , wherein the anodic oxidation is carried out with oxalic acid as an electrolyte and at a formation voltage of 30 to 60 V.
3. The mold composed of anodic oxidized porous alumina according to claim 1 , wherein the anodic oxidation is carried out with sulfuric acid as an electrolyte and at a formation voltage of 20 to 30 V.
4. The mold composed of anodic oxidized porous alumina according to claim 1 , wherein the mold has a pore period of 50 to 600 nm and a pore depth of 100 nm or more.
5. The mold composed of anodic oxidized porous alumina according to claim 1 , wherein repeating the anodic oxidation and the pore diameter enlargement treatment are terminated with the anodic oxidation.
6. A method for producing an anti-reflective film having a refractive index continuously changed and then reducing reflectance comprising:
forming unevenness on a surface of a polymer molding material by molding shape with the mold according to claim 1 .
7. An anti-reflective film having a refractive index continuously changed and then reducing reflectance produced with the mold according to claim 1 .