Powder coating composition for PC strand coating, coating method, and coating film
View Patent ↗A powder coating composition for PC strand coating which, when used for the coating of a PC strand, can advantageously form a coating film having an even thickness at low cost without causing uneven thickness or stringness is disclosed. The powder coating composition of this invention for PC strand coating is characterized by having a melt viscosity of 3,000-15,000 poise.
1. A powder coating composition for prestressed concrete (PC) strand coating, wherein
the powder coating composition has a melt viscosity of 3000 to 15000 poise,
the powder coating composition comprises an epoxy resin and a curing agent,
the curing agent is a diglycidylether-modified bisphenol A,
the curing agent has a phenolic hydroxy equivalent within a range of 500 to 800 g/eq,
a mixing ratio of the epoxy resin and the curing agent, which is an equivalent ratio of a phenolic hydroxy equivalent of the curing agent to an epoxy equivalent of the epoxy resin, is within a range of 0.7/1.0 to 1.5/1.0, and
the powder coating composition is suitable for coating PC strands.
2. The powder coating composition of claim 1 wherein the epoxy resin has epoxy equivalents of 1000 to 4700 g/eq.
3. The powder coating composition of claim 2 , wherein the powder coating composition comprises a resin obtained by partially-reacting an epoxy resin with a phenolic curing agent.
4. A coating method for PC strand comprising a step of continuously-coating of the powder coating composition of claim 2 in finely-powdered form on a PC strand under a closed condition.
5. The powder coating composition of claim 1 wherein the powder coating composition comprises a resin obtained by partially-reacting an epoxy resin with a phenolic curing agent.
6. The powder coating composition of claim 5 wherein the powder coating composition comprises a resin obtained by partially-reacting an epoxy resin having epoxy equivalents of 1000 to 2000 g/eq and a phenolic curing agent.
7. A coating method for PC strand comprising a step of continuously-coating of the powder coating composition of claim 6 in finely-powdered form on a PC strand under a closed condition.
8. A coating method for PC strand comprising a step of continuously-coating of the powder coating composition of claim 5 in finely-powdered form on a PC strand under a closed condition.
9. A coating method for a prestressed concrete (PC) strand comprising a step of continuously-coating of the powder coating composition of claim 1 in finely-powdered form on a PC strand under a closed condition.
10. The coating method of claim 9 wherein the coating method is an immersion coating method.
11. A coating film obtained by the coating method of claim 10 .
12. The coating film of claim 11 which has a breaking elongation percentage of not less than 30%.
13. The coating method of claim 9 wherein the coating method is an electrostatic immersion coating method.
14. A coating film obtained by the coating method of claim 13 .
15. The powder coating composition of claim 1 , wherein the epoxy resin has not less than 90% of a content of terminal epoxy groups based on a total number of epoxy groups.