Soft polypropylene composition with soft touch feeling

1. Propylene polymer composition comprising:

(a) at least 74.0 to 86.0 wt. % of an heterophasic propylene copolymer based on the total amount of propylene polymer composition comprising

(i) 50.0 to 70.0 wt-% of a polypropylene copolymer based on the total amount of the heterophasic propylene copolymer, wherein the polypropylene copolymer is a copolymer of propylene and an amount of 1.0 to not more than 8.0 wt.-% of a comonomer selected from the group consisting of ethylene, C4 α-olefin, C6 α-olefin, C7 α-olefin, C8 α-olefin C9 α-olefin, C10 α-olefin, C11 α-olefin, C12 α-olefin, C13 α-olefin, C14 α-olefin, C15 α-olefin, C16 α-olefin, C17 α-olefin, C18 α-olefin, C19 α-olefin, C20 α-olefin and mixtures thereof, and

(ii) 30.0 to 50.0 wt.-% of an elastomeric copolymer based on the total amount of the heterophasic propylene copolymer, said elastomeric copolymer being an elastomeric copolymer of ethylene and in an amount of 60-80wt.-%, of at least one α-olefin comonomer selected from the group consisting of propylene, 1-butene, 1-pentene, 1-hexene, 1-heptene and 1-octene, and wherein the heterophasic propylene copolymer has a melt flow rate of 0.4-1.0 g/10 min

(b) 10 to 30 wt.-% based on the total amount of propylene polymer composition of an ethylene C2 to C8 alkyl acrylate copolymer, having 17-27 wt.-% of C2-C8 acrylate and an MFR of 1.5 to 4.0 g/10 min, and

(c) 0.1 to 5.0 wt.-% of units derived from at least bifunctionally unsaturated monomer(s) and/or at least multifunctionally unsaturated low molecular weight polymer(s) based on the total amount of propylene polymer composition, aid bifunctionally unsaturated monomer(s) being selected from the group consisting of divinylaniline, divinylpentane, divinylpropane, allyl acrylate, allyl methacrylate, allyl methyl maleate allyl vinyl ether, 1,3-butadiene, chloroprene, cyclohexadiene, cyclopentadiene, 2,3-dimethylbutadiene, heptadiene, hexadiene, isoprene and 1,4-pentadiene, aliphatic bis(maleimide), aromatic and/or aliphatic bis(citraconimide) and mixtures of those unsaturated monomers, and said at least multifunctionally unsaturated low molecular weight polymer having M n ≦10,000 g/mol and being a polybutadiene having more than 50% of the butadiene in the 1,2 vinyl configuration,

wherein

the propylene polymer composition has a gel content determined as the xylene hot insoluble fraction content of at least 0.25 wt.-% to equal or below 1.00 wt.-%;

wherein said propylene polymer composition has a tensile modulus of 152 to below 200 MPa measured according to ISO 527-3 (cross head speed=50 mm/min);

a strain hardening SH 3.0/2.5 (at a Hencky strain rate of 3 s −1 ) of at least 0.5-1.03; and;

high impact strength of at least 80 to 105.2 kJ/m 2 at −20° C.

2. Propylene polymer composition according to claim 1 , wherein the polypropylene copolymer is the matrix of said heterophasic propylene copolymer and the elastomeric copolymer is the amorphous part of said heterophasic propylene copolymer.

3. Propylene polymer according to claim 1 , wherein the comonomer of the polypropylene copolymer is ethylene.

4. Propylene polymer composition according to claim 1 , wherein the polypropylene copolymer is bimodal.

5. Propylene polymer composition according to claim 1 , wherein the elastomeric copolymer is an ethylene propylene rubber (EPR).

6. Propylene polymer composition according to claim 1 , wherein the intrinsic viscosity of the elastomeric copolymer, determined as the intrinsic viscosity of the acetone precipitated fraction of the xylene soluble fraction, IV of AM, is in the range of 1.0 to 4.0 dl/g.

7. Propylene polymer composition according to claim 1 , wherein:

the comonomer of the polypropylene copolymer is selected from the group consisting of ethylene and C4 α-olefin, C5 α-olefin, C6 α-olefin, C7 α-olefin, C8 α-olefin, C9 α-olefin, C10 α-olefin, C11 α-olefin, C12 α-olefin, C13 α-olefin, C14 α-olefin, C15 α-olefin, C16 α-olefin, C17 α-olefin, C18 α-olefin, C19 α-olefin, and mixtures thereof, and,

the comonomer of the elastomeric copolymer if selected from the group consisting of propylene, 1-butene, 1-pentene, 1-hexene, 1-heptene, and mixtures thereof.

8. Propylene polymer composition according to claim 1 , wherein the C2 to C8 alkyl of the ethylene C2 to C8 alkyl acrylate copolymer is selected from the group consisting of methyl, ethyl, and butyl.

9. Propylene polymer composition according to claim 1 , wherein the ethylene C2 to C8 alkyl acrylate copolymer is ethylene butyl-acrylate (EBA).

10. Propylene polymer composition according to claim 1 , wherein the bifunctionally unsaturated monomers used for the units are selected from the group consisting of divinyl compounds, allyl compounds and dienes.

11. Propylene polymer composition according to claim 1 , wherein the composition has an MFR 2 (230° C.) measured according to ISO 1133 of not more than 5.00 g/10 min.

12. Propylene polymer composition according to claim 1 used in the manufacture of films, injection molded parts and flexible pipes.

13. Process for the manufacture of a propylene polymer composition comprising:

providing a heterophasic mixture of a polypropylene copolymer

and an elastomeric copolymer of ethylene and at least one α-olefin comonomer selected form the group consisting of propylene, 1-butene, 1-pentene, 1-hexene, 1-heptene and 1-octene,

providing an ethylene C2 to C8 alkyl acrylate copolymer, and further comprising the steps of:

(a) mixing the heterophasic mixture of polypropylene copolymer and elastomeric copolymer and said ethylene C2 to C8 alkyl acrylate copolymer,

(b) adding bifunctionally unsaturated and/or multifunctionally unsaturated compounds, and

(c) extruding said mixture

wherein the propylene polymer composition comprises:

(α) at least 74.0 to 86.0 wt.-% of an heterophasic propylene copolymer based on the total amount of propylene polymer composition comprising

(i) 50.0 to 70.0 wt.-% of a polypropylene copolymer based on the total amount of the heterophasic propylene copolymer, wherein the polypropylene copolymer is a copolymer of propylene and an amount of 1.0 to not more than 8.0 wt.-% of a comonomer selected from the group consisting of ethylene, C4 α-olefin, C5 α-olefin, C6 α-olefin, C7 α-olefin, C8 α-olefin, C9 α-olefin, C10 α-olefin, C11 α-olefin, C12 α-olefin, C13 α-olefin, C14 α-olefin, C15 α-olefin, C16 α-olefin, C17 α-olefin, C18 α-olefin, C19 α-olefin, C20 α-olefin and mixtures thereof, and

(ii) 30.0 to 50.0 wt.-% of an elastomeric copolymer based on the total amount of the heterophasic propylene copolymer, said elastomeric copolymer being an elastomeric copolymer of ethylene and in an amount of 60-80 wt.-% of at least one α-olefin comonomer selected from the group consisting of propylene, 1-butene, 1-pentene, 1-hexene, 1-heptene and 1-octene, and wherein the heterophasic propylene copolymer has a melt flow rate of 0.4 to 1.0 g/10 min, and

(β) 10 to 30 wt.-% based on the total amount of propylene polymer composition of an ethylene C2 to C8 alkyl acrylate copolymer, having 17-27 wt.-% C2-C8 acrylate and an MFR of 1.5 to 4.0 g/10 min, and

(γ) 0.1 to 5.0 wt.-% of units derived from at least bifunctionally unsaturated monomer(s) and/or at least multifunctionally unsaturated low molecular weight polymer(s) based on the total amount of propylene polymer composition, said bifunctionally unsaturated monomer(s) being selected from the group consisting of divinylaniline, divinylpentane, divinylpropane, allyl acrylate, allyl methacrylate, allyl methyl maleate, allyl vinyl ether, 1,3-butadiene, chloroprene, cyclohexadiene, cyclopentadiene, 2,3-dimethylbutadiene, heptadiene, hexadiene, isoprene and 1,4-pentadiene, aliphatic bis(maleimide), aromatic and/or aliphatic bis(citraconimide) and mixtures of thaw unsaturated monomers, and said at least multifunctionally unsaturated low molecular weight polymer having M n ≦10,000 g/mol mol and being a polybutadiene having more than 50% of the butadiene in the 1,2 vinyl configuration,

wherein the propylene polymer composition has a gel determined as the xylene hot insoluble fraction content of at least 0.25 wt.-% to equal or below 1.00 wt.-%,

wherein the propylene polymer composition has a tensile modulus of 152 to below 200 MPa measured according to ISO 527-3 (cross head speed=50 mm/min);

a strain hardening SH 3.0/2.5 (at a Hencky strain rate of 3 s −1 ) of at least 0.5-1.03; and;

high impact strength of at least 80-105.2 kJ/m 2 at −20° C.

14. Process according to claim 13 , wherein said heterophasic mixture of the polypropylene copolymer and the elastomeric copolymer is produced by the steps comprising:

(a) polymerizing propylene and further comonomer(s) in at least one reactor to obtain the polypropylene copolymer, and

(b) transferring said polypropylene copolymer in a further reactor, producing an elastomeric copolymer by polymerizing propylene and further comonomer(s) in the presence said polypropylene copolymer to obtain the heterophasic mixture.

15. Process according to claim 13 , wherein step (b) is carried out by using at least bifunctionally unsaturated monomer(s) and a thermally decomposing free radical-forming agent.

16. Process according to claim 13 , wherein said heterophasic mixture of polypropylene and elastomeric copolymer is produced by comprising the steps

(a) polymerizing propylene and further comonomer(s) in a loop reactor followed by a gas phase reactor, to obtain the polypropylene copolymer, and

(b) transferring said polypropylene copolymer in a further gas phase reactor,

(c) producing an elastomeric copolymer by polymerizing propylene and further comonomer(s) in the presence said polypropylene copolymer to obtain the heterophasic mixture.

17. Films, injection molded parts of flexible pipes comprising a propylene composition comprising:

(a) at least 74.0 to 88.0 wt.-% of an heterophasic propylene copolymer based on the tot amount of propylene polymer composition comprising

(i) 50.0 to 70.0 wt.-% of a polypropylene copolymer based on the total amount of the heterophasic propylene copolymer, wherein the polypropylene copolymer is a copolymer of propylene and an amount of 1.0 to not more than 8.0 wt.-% of a comonomer selected from the group consisting of ethylene, C4 α-olefin, C5 α-olefin, C6 α-olefin, C7 α-olefin, C8 α-olefin, C9 α-olefin, C10 α-olefin, C11 α-olefin, C12 α-olefin, C13 α-olefin, C14 α-olefin, C15 α-olefin, C16 α-olefin, C17 α-olefin, C18 α-olefin, C19 α-olefin, C20 α-olefin and mixtures thereof, and

(ii) 30.0 to 50.0 wt.-% of an elastomeric copolymer based on the total amount of the heterophasic propylene copolymer, said elastomeric copolymer being an elastomeric copolymer of ethylene and in an amount of 60-80 wt.-% of at least α-olefin comonomer selected from the group consisting of propylene, 1-butene, 1-pentene, 1-hexene, 1-heptene and 1-octene, and wherein the heterophasic propylene copolymer has a melt flow rate of 0.4-1.0 g/10, and

(b) 10 to 30 wt.-% based on the total amount of propylene polymer composition of an ethylene C2 to C8 alkyl acrylate copolymer, having 17-27 wt.-% of C2-C8 acrylate and an MFR of 1.5 to 4.0 g/10 min, and

(c) 0.1 to 5.0 wt.-% of units derived from at least bifunctionally unsaturated monomer(s) and/or at least multifunctionally unsaturated low molecular weight polymer(s) based on the total amount of propylene polymer composition, said bifunctionally unsaturated monomer(s) being selected from the group consisting of divinylaniline, divinylpentane, divinylpropane, allyl acrylate, allyl methacrylate, allyl methyl maleate, allyl vinyl ether, 1,3-butadiene, chloroprene, cyclohexadiene, cyclopentadiene, 2,3-dimethylbutadiene, heptadiene, hexadiene, isoprene and 1,4-pentadiene, aliphatic bis(maleimide), aromatic and/or aliphatic bis(citraconimide) and mixtures of these unsaturated monomers, and said at least multifunctionally unsaturated low molecular weight polymer having M n ≦10,000 g/mol and being a polybutadiene having more than 50% of the butadiene in the 1,2 vinyl configuration

wherein the propylene polymer composition has a gel content of at least 0.25 wt.-% to equal or below 1.00 wt.-% determined as the xylene hot insoluble fraction,

wherein the propylene polymer composition has a tensile modulus of 152 to below 200 MPa measured according to ISO 527-3 (cross head speed=50 mm/min);

a strain hardening SH 3.0/2.5 (at a Hencky strain rate of 3 s −1 ) of at least 0.5-1.03; and;

high impact strength of at least 60-105.2 kJ/m 2 at −20° C.