Active material for lithium secondary battery, lithium secondary battery, and method for producing the same
View Patent ↗The active material for a lithium secondary battery includes a solid solution of a lithium transition metal composite oxide having an α-NaFeO 2 type crystal structure, in which the composition ratio of Li, Co, Ni, and Mn contained in the solid solution satisfies Li 1+(1/3)x Co 1−x−y Ni (1/2)y Mn (2/3)x+(1/2)y (x+y≦1, 0≦y and 1−x−y=z); in an Li[Li 1/3 Mn 2/3 ]O 2 (x)-LiNi 1/2 Mn 1/2 O 2 (y)-LiCoO 2 (z) type ternary phase diagram, (x, y, z) is represented by values in a range present on or within a line of a heptagon (ABCDEFG) defined by the vertexes; point A(0.45, 0.55, 0), point B(0.63, 0.37, 0), point C(0.7, 0.25, 0.05), point D(0.67, 0.18, 0.15), point E(0.75, 0, 0.25), point F(0.55, 0, 0.45), and point G(0.45, 0.2, 0.35); and the intensity ratio between the diffraction peaks on (003) plane and (104) plane measured by X-ray diffractometry before charge-discharge is I (003) /I (104) ≧1.56 and at the end of discharge is I (003) /I (104) >1.
1. An active material for a lithium secondary battery comprising:
a solid solution of a lithium transition metal composite oxide having an α-NaFeO 2 -type crystal structure,
wherein a composition ratio of Li, Co, Ni, and Mn contained in the solid solution satisfies Li 1+(1/3)x Co 1-x-y Ni (1/2)y Mn (2/3)x+(1/2)y where x+y≦1, 0≦y and 1−x−y=z;
in an Li[Li 1/3 Mn 2/3 ]O 2 (x)-LiNi 1/2 Mn 1/2 O 2 (y)-LiCoO 2 (z) type ternary phase diagram, (x, y, z) is represented by values in a range present on or within a line of a heptagon (ABCDEFG) defined by vertexes; point A(0.45, 0.55, 0), point B(0.63, 0.37, 0), point C(0.7, 0.25, 0.05), point D(0.67, 0.18, 0.15), point E(0.75, 0, 0.25), point F(0.55, 0, 0.45), and point G(0.45, 0.2, 0.35); and
an intensity ratio between diffraction peaks on (003) plane and (104) plane measured by X-ray diffractometry before charge-discharge is I (003) /I (104) ≧1.56 and at an end of discharge is I (003) /I (104) >1.
2. The active material for a lithium secondary battery according to claim 1 , wherein a dischargeable electric quantity after being charged at 4.3 V (vs. Li/Li + ) or lower is 180 mAh/g or higher.
3. An active material for a lithium secondary battery, comprising:
a solid solution of a lithium transition metal composite oxide having an α-NaFeO 2 -type crystal structure,
wherein a composition ratio of Li, Co, Ni, and Mn contained in the solid solution satisfies Li 1+(1/3)x Co 1-x-y Ni (1/2)y Mn (2/3)x+(1/2)y where x+y≦1, 0≦y and 1−x−y=z;
in an Li[Li 1/3 Mn 2/3 ]O 2 (x)-LiNi (2/3) Mn 1/2 O 2 (y)-LiCoO 2 (z) type ternary phase diagram, (x, y, z) is represented by values in a range present on or within a line of a heptagon (ABCDEFG) defined by vertexes; point A(0.45, 0.55, 0), point B(0.63, 0.37, 0), point C(0.7, 0.25, 0.05), point D(0.67, 0.18, 0.15), point E(0.75, 0, 0.25), point F(0.55, 0, 0.45), and point G(0.45, 0.2, 0.35); and
an intensity ratio between diffraction peaks on (003) plane and (104) plane measured by X-ray diffractometry at an end of discharge is I (003) /I (104) >1 and a dischargeable electric quantity after being charged at 4.3 V (vs. Li/Li + ) or lower is 177 mAh/g or higher.
4. The active material for a lithium secondary battery according to claim 1 or 3 , wherein (x, y, x) is represented by values in a range present on or within a line of a tetragon (HIJK) defined by the vertexes; point H(0.6, 0.4, 0), point I(0.67, 0.13, 0.2), point J(0.7, 0, 0.3), and point K(0.55, 0.05, 0.4).
5. The active material for a lithium secondary battery according to claim 4 , wherein the dischargeable electric quantity after being charged at 4.3 V (vs. Li/Li + ) or lower is 200 mAh/g or higher.
6. The active material for a lithium secondary battery according to claim 1 or 3 , wherein the solid solution of lithium-transition metal composite oxide has a diffraction peak observed near 20 to 30° in X-ray diffractometry using CuKα radiation for monoclinic Li[Li 1/3 Mn 2/3 ]O 2 before charge-discharge and an intensity of the diffraction peak is about 4 to 7% of an intensity of the diffraction peak of the (003) plane.
7. The active material for a lithium secondary battery according to claim 1 or 3 , wherein the solid solution of lithium-transition metal composite oxide is produced by a coprecipitation method.
8. A method for producing an active material for a lithium secondary battery according claim 1 or 3 , comprising producing the solid solution of lithium-transition metal composite oxide through the steps of producing a precursor by coprecipitation of a compound containing Co, Ni, and Mn in a solvent, mixing the precursor and a lithium compound, and calcining the mixture.
9. A lithium secondary battery comprising a positive electrode containing the active material for a lithium secondary battery according to claim 1 or 3 .
10. A method for producing the lithium secondary battery according to claim 9 by employing a charging method where the positive electrode upon charging has a maximum achieved potential of 4.3 V (vs. Li/Li + ) or lower, the method comprising the step of charging to reach at least a region with relatively flat fluctuation of potential appearing in a positive electrode potential region exceeding 4.3 V (vs. Li/Li + ) but lower than 4.8 V (vs. Li/Li + ).