Hearth roll in a continuous annealing furnace and its production method
View Patent ↗The hearth roll for a continuous annealing furnace is able to suppress the occurrence of buildup on the hearth roll surface and able to be stably used for a long period under the high temperature environment. The hearth roll has a cermet coating comprised 50 to 90 vol % of ceramic and the balance of a heat resistant alloy on its surface, the ceramic containing Cr 3 C 2 : over 50 to 90 vol %, Al 2 O 3 : 1 to 40 vol %, Y 2 O 3 : 0 to 3 vol %, and ZrB 2 : 0 to 40 vol % and having a balance of unavoidable impurities and pores, the heat resistant alloy containing Cr: 5 to 20 mass %, Al: 5 to 20 mass %, and one or both of Y and Si: 0.1 to 6 mass % and has a balance of one or both of Co and Ni and unavoidable impurities.
1. A hearth roll for a continuous annealing furnace, the hearth roll having a cermet coating comprising 60 to 80 vol % of a ceramic and a balance of a heat resistant alloy on a surface of the hearth roll, wherein
the ceramic comprises:
Cr 3 C 2 : over 55 to 90 vol %,
Al 2 O 3 : 1 to 40 vol %,
Y 2 O 3 : 0.5 to 3 vol %,
ZrB 2 : 0 to 40 vol %, and
a balance of unavoidable impurities and pores, and
the heat resistant alloy comprises:
Cr: 5 to 20 mass %,
Al: 5 to 20 mass %,
one or both of Y and Si: 0.1 to 6 mass %, and
a balance of one or both of Co and Ni and unavoidable impurities.
2. The hearth roll for a continuous annealing furnace as set forth in claim 1 , wherein
the heat resistant alloy further comprises one or both of
Nb: 0.1 to 10 mass % and
Ti: 0.1 to 10 mass %.
3. The hearth roll for a continuous annealing furnace as set forth in claim 1 , wherein the Cr 3 C 2 in the ceramic has a particle size of 1 to 10 μm.