Zinc-based plated steel sheet excellent in surface electrical conductivity having primary rust preventive thin film layer
View Patent ↗A zinc or zinc alloy plated steel sheet expressing a performance provided with both corrosion resistance and surface conductivity is provided. The zinc or zinc alloy plated steel sheet of the present invention is a zinc or zinc alloy plated steel sheet having an arithmetic average roughness Ra of a zinc-plated layer surface defined by JIS B 0601, obtained by a stylus-type surface roughness meter defined by JIS B 0651, of 0.3 μm to 2.0 μm and a maximum peak height Rp of 4.0 μm to 20.0 μm, wherein the arithmetic average roughness Ra (peak) obtained by measuring a range of evaluation length of 20 μm of peak parts of 80% or more of the Rp by an electron beam 3D roughness analyzer is 70% or more of the arithmetic average roughness Ra (average) obtained by measuring a range of evaluation length of 20 μm of parts of a height of ±20% about an average line, obtained by a stylus-type surface roughness meter, by an electron beam 3D roughness analyzer.
1. A rust preventive coated zinc or zinc alloy plated steel sheet superior in surface conductivity, comprising:
a zinc or zinc alloy plated steel sheet coated with a thin-film primary rust preventive coating layer;
the thin-film primary rust preventive coating layer having an average thickness of 0.2 μm to 5.0 μm,
the zinc or zinc alloy plated steel sheet having an arithmetic average roughness of a zinc plated layer surface, Ra, of 0.3 μm to 2.0 μm, as defined by JIS B 0601, obtained using a stylus-type surface roughness meter, as defined by JIS B 0651, and a maximum peak height, Rp, of 4.0 μm to 20.0 μm, wherein
the arithmetic average roughness of a zinc plated layer surface, Ra (peak), obtained by measuring a range of evaluation length of 20 μm of peak parts of 80% or more of the Rp by an electron beam 3D roughness analyzer is 70% or more of the arithmetic average roughness, Ra (average), obtained by measuring a range of evaluation length of 20 μm of parts of a height of ±20% about an average line, obtained by a stylus-type surface roughness meter, by an electron beam 3D roughness analyzer.
2. The rust preventive coated zinc or zinc alloy plated steel sheet as set forth in claim 1 , wherein
the area of the parts where the arithmetic average roughness Ra 5(peak) obtained by measuring a range of evaluation length of 20 μm of peak parts of 80% or more of the Rp defined by JIS B 0601, obtained by a stylus-type surface roughness meter, by an electron beam 3D roughness analyzer is less than 70% of the arithmetic average roughness Ra (average) obtained by measuring a range of evaluation length of 20 μm of parts of a height of ±20% about an average line, obtained by a stylus-type surface roughness meter, by an electron beam 3D roughness analyzer is 5% or less of the zinc-plated surface area as a whole.
3. The rust preventive coated zinc or zinc alloy plated steel sheet as set forth in claim 1 or 2 , wherein the arithmetic average roughness Ra (peak) obtained by measuring a range of evaluation length of 20 μm of peak parts of 80% or more of the Rp defined by JIS B 0601, obtained by a stylus-type surface roughness meter, by an electron beam 3D roughness analyzer is 0.03 μm to 1.0 μm.