Method of regenerating exhaust gas treatment catalyst and exhaust gas treatment catalyst obtained by the method
View Patent ↗Provided is a method of regenerating an exhaust gas treatment catalyst 11 having ash adhered to a surface thereof. The method includes a crushing step S 1 in which the exhaust gas treatment catalyst 11 is crushed such that 70 to 95 wt % of the whole exhaust gas treatment catalyst 11 becomes coarse pieces 12 having a size exceeding a threshold size S (any value in a range of 0.105 to 1.0 mm); a separating step S 2 in which the fragments obtained by crushing the exhaust gas treatment catalyst 11 are separated into the coarse pieces 12 having a size exceeding threshold size S and fine particles 13 having a size not larger than the threshold size S; a pulverizing step S 3 in which the coarse pieces 12 thus separated are pulverized to a fine powder having an average particle diameter of not larger than 0.1 mm; a kneading step S 4 and a molding step S 5 in which the fine powder is kneaded with other raw materials and molded into an exhaust gas treatment catalyst; and a drying step S 6 and a calcining step S 7 in which the molded precursor is dried and calcined to thus obtain a regenerated exhaust gas treatment catalyst 14.
1. A method of regenerating an exhaust gas treatment catalyst having ash adhered to a surface thereof, the method characterized by comprising:
a crushing step of crushing the exhaust gas treatment catalyst that has been used and has ash adhered to the surface thereof;
a separating step of separating the crushed exhaust gas treatment catalyst into coarse pieces having a size exceeding a threshold size S and fine particles having a size not larger than the threshold size S;
a pulverizing step of pulverizing the separated coarse pieces into a fine powder;
a molding step of molding the pulverized fine powder as a raw material into an exhaust gas treatment catalyst without using the separated fine particles as the raw material; and
a calcining step of calcining a molded precursor of the exhaust gas treatment catalyst,
wherein the threshold size S has a value not smaller than 0.105 mm.
2. The method according to claim 1 , wherein
the crushing step is a step in which the exhaust gas treatment catalyst that has been used is crushed such that 70 to 95 wt % of the whole exhaust gas treatment catalyst that has been used becomes the coarse pieces having a size exceeding the threshold size S.
3. The method according to claim 2 , wherein
the threshold size S has a value not larger than 1.0 mm.
4. The method of according to claim 1 , wherein
the pulverizing step is a step in which the coarse pieces is pulverized such that the fine powder has an average particle diameter not larger than 0.1 mm.
5. The method according to claim 1 , further comprising a treating step of treating exhaust gas from burned coal using the exhaust gas treatment catalyst after the calcining step.
6. The method according to claim 5 , wherein the treating step is a step of treating nitrogen oxide in the exhaust gas.
7. The method according to claim 1 , wherein
a percentage of Fe 2 O 3 in the coarse pieces separated in the separating step is 0.25 wt % or less.
8. The method according to claim 1 , wherein
the exhaust gas treatment catalyst is made of at least one metal oxide from titanium oxide (TiO 2 ), tungsten oxide (WO 3 ), and vanadium oxide (V 2 O 5 ).
9. The method of regenerating an exhaust gas treatment catalyst according to claim 1 , wherein
the crushing step is a step in which the exhaust gas treatment catalyst that has been used and has the ash adhered to the surface thereof is crushed without being washed.