Polyolefin composition comprising crosslinkable polyolefin with silane groups, silanol condensation catalyst and pigment
View Patent ↗The present invention is directed to particular titanium dioxide containing compositions which allow the retention of a high crosslinking performance of a polyolefin composition comprising a crosslinkable polyolefin with hydrolysable silane groups, a Brönstedt acid silanol condensation catalyst and said titanium dioxide containing composition. The retention of the high crosslinking performance is shown by a difference in torque measured at 120° C. of 40 Nm or higher.
1. A polyolefin composition comprising
(i) a crosslinkable polyolefin with hydrolysable silane groups (A),
(ii) a silanol condensation catalyst (B) which is a Brönstedt acid (B), and
(iii) a titanium dioxide containing composition (C),
characterized in that the difference between the highest torque value, when the crosslinking is completed, and the lowest torque value, before the crosslinking starts, both values measured at 120° C., is 40 Nm or higher.
2. Polyolefin composition according to claim 1 , wherein the difference in torque measured at 120° C. is 44 Nm or higher.
3. Polyolefin composition according to claim 1 , wherein the difference in torque measured at 120° C. is 45 Nm or higher.
4. Polyolefin composition according to claim 1 , characterized in that said titanium dioxide containing composition does not comprise a coating containing silicon and the concentration of the titanium dioxide in said titanium dioxide containing composition is at least 93 wt %.
5. Polyolefin composition according to claim 4 , wherein the concentration of the titanium dioxide in said titanium dioxide containing composition is at least 97 wt %.
6. Polyolefin composition according to claim 1 , wherein the titanium dioxide in said titanium dioxide containing composition (C) is not coated.
7. Polyolefin composition according to claim 1 , characterized in that the titanium dioxide in said titanium dioxide containing composition is coated, which coating contains silicon, and the concentration of the titanium dioxide in said titanium dioxide containing composition is at least 97 wt %.
8. Polyolefin composition according to claim 1 , wherein the crosslinkable polyolefin with hydrolysable silane groups (A) comprises a polyethylene with hydrolysable silane groups.
9. Article comprising the polyolefin composition according to claim 1 .
10. Article according to claim 9 , wherein the article is a wire or cable.
11. Polyolefin composition according to claim 4 , wherein the titanium dioxide in said titanium dioxide containing composition (C) is not coated.