Method of preparing a transparent polymer material comprising a thermoplastic polycarbonate and surface-modified mineral nanoparticles
View Patent ↗A method of preparing a transparent polymer material includes i) obtaining composite nanoparticles having mineral nanoparticles at least partially coated with at least one monomer and/or at least one polymer suitable for promoting physicochemical interactions at the interface between the mineral nanoparticles and a thermoplastic polycarbonate matrix, the mineral nanoparticles being surface-modified by the monomer and/or the polymer, either directly by grafting or directly by adsorption of the monomer and/or polymer onto the surface of the mineral nanoparticles; or via a coupling agent selected from a chlorosilane or an organosilane including a functional group that is capable of reacting by a radical pathway. The composite nanoparticles obtained in step i) are mixed with the thermoplastic polycarbonate matrix in the molten state to obtain the transparent polymer material.
1. A method of preparing a transparent polymer material, the method comprising the following steps:
i) obtaining composite nanoparticles comprising mineral nanoparticles at least partially coated with at least one monomer, wherein the monomer is selected from the group consisting of styrene, methyl methacrylate, butyl acrylate, bisphenol A, phosgene, diphenyl carbonate, acrylamide, and combinations thereof
at least one polymer, wherein the polymer either one of selected from the group consisting of polystyrene, polycarbonate, polymethyl methacrylate, polybutyl acrylate, polyacrylamide, and combinations thereof, or
a copolymer of the group consisting of styrene, polycarbonate monomer, methyl methacrylate, butyl acrylate, bisphenol A, acrylamide, and combinations thereof
and combinations thereof, suitable for promoting physicochemical interactions at the interface between the mineral nanoparticles and a thermoplastic polycarbonate matrix, said mineral nanoparticles being surface-modified by said monomer, said polymer, and combinations thereof:
directly by grafting or directly by adsorption of the monomer, the polymer, and combinations thereof, onto the surface of said mineral nanoparticles
wherein said mineral nanoparticles being surface-modified by said monomer, said polymer, and combinations thereof, directly by creating a hydrogen bond or creating Van der Waals bond, between the mineral nanoparticles from one hand, and the monomer, the polymer, and combinations thereof, from the other hand; and
ii) mixing the composite nanoparticles obtained in step i) with the thermoplastic polycarbonate matrix in a molten state to obtain said transparent polymer material, said transparent polymer material including at most 10% by weight of said composite nanoparticles, wherein said transparent polymer material is a material through which an image is observed with no loss contrast.
2. The method according to claim 1 , wherein the dimension of the mineral nanoparticles is at most 300 nm.
3. The method according to claim 1 , wherein the mineral nanoparticles are selected from the group consisting of nanoparticles of alkaline-earth metal carbonates, alkaline-earth metal sulfates, metallic oxides, oxides of metalloids, siloxanes, and combinations thereof.
4. The method according to claim 3 , wherein the mineral nanoparticles are selected from the group consisting of nanoparticles of calcium carbonate, barium sulfate, alumina, trisilanolphenyl polyhedral silsesquioxane (TP-POSS), zinc oxide, silicon dioxide, titanium dioxide, and combinations thereof.
5. The method according to claim 1 , wherein the monomer of step i) is grafted to the surface of said nanoparticles, then the said monomer is polymerized.
6. The method according to claim 1 , wherein the mixture of step ii) is produced using an extruder.
7. A transparent polymer material obtained by the method defined in claim 1 .
8. A method of manufacture of optical articles for automobile glass, said method comprising the step of:
forming said optical articles for automobile glass with said polymer material according to claim 7 .
9. A method of manufacture of optical articles of the sighting instrument lens, helmet visor or ophthalmic lens, said method comprising the step of:
forming said optical articles of the sighting instrument lens, helmet visor or ophthalmic lens with said polymer material according to claim 7 .
10. A method of manufacture of optical articles with a thickness of at most 15 mm, said method as comprising the step of:
forming said optical articles with a thickness of at most 15 mm with said polymer material according to claim 7 .
11. The method according to claim 2 , wherein the dimension of the mineral nanoparticles is at most 100 nm.
12. The method according to claim 2 , wherein the dimension of the mineral nanoparticles is in the range 10 nm to 70 nm.
13. The polymer material according to claim 7 , wherein said polymer material is at most 5% by weight of mineral nanoparticles.
14. The polymer material according to claim 7 , wherein said polymer material is a quantity of the order of 1% by weight of mineral nanoparticles.
15. A method of manufacture of optical articles with a thickness in the range 0.1 mm to 5 mm, said method as comprising the step of:
forming said optical articles with a thickness of at most 15 mm with said polymer material according to claim 7 .
16. A method of manufacture of optical articles with a thickness in the range 0.5 mm to 4 mm, said method as comprising the step of:
forming said optical articles with a thickness of at most 15 mm with said polymer material according to claim 7 .
17. A method of preparing a transparent polymer material, the method comprising the following steps:
i) obtaining composite nanoparticles comprising mineral nanoparticles at least partially coated with at least one monomer, at least one polymer, and combinations thereof, suitable for promoting physicochemical interactions at the interface between the mineral nanoparticles and a thermoplastic polycarbonate matrix, said mineral nanoparticles being surface-modified by said monomer, said polymer, and combinations thereof:
via an organosilane coupling agent including a functional group that is capable of reacting by a radical pathway and at least one hydrolysable functional group selected from an alkoxy and carboxy group, wherein the organosilane is vinyl trimethoxysilane or methacryloxypropyl trimethoxysilane; and
ii) mixing the composite nanoparticles obtained in step i) with the thermoplastic polycarbonate matrix in a molten state to obtain said transparent polymer material, said transparent polymer material including at most 10% by weight of said composite nanoparticles,
wherein
the monomer of step i is selected from the group consisting of styrene, methyl methacrylate, butyl acrylate, bisphenol A, phosgene, diphenyl carbonate, acrylamide, and combinations thereof,
the polymer of step i is selected from the group consisting of polystyrene, polycarbonate, polymethyl methacrylate, polybutyl acrylate, polyacrylamide, a copolymer of styrene, a copolymer of polycarbonate, a copolymer of methyl methacrylate, a copolymer of butyl acrylate, a copolymer of bisphenol A, a copolymer of acrylamide, and combinations thereof, and
the functional group of the organosilane is selected from the group consisting of acrylate, methacrylate, vinyl, and allyl, wherein said transparent polymer material is a material through which an image is observed with no loss contrast.
18. The method of preparing a transparent polymer material according to claim 17 , wherein said mineral nanoparticles being surface-modified by said monomer and/or said polymer directly by creating hydrogen bond, between the mineral nanoparticles from one hand, and the monomer and/or the polymer from the other hand.