Magnetic recording medium and manufacturing method of the same
View Patent ↗To provide a magnetic recording medium enabling excellent magnetic recording reproduction characteristics to be exhibited with the spacing loss reduced and a manufacturing method of the medium, a method of manufacturing a magnetic recording medium of the invention is to manufacture a magnetic recording medium having a magnetic recording layer of a granular structure having nonmagnetic boundary portions between pillar-shaped magnetic particles on a nonmagnetic substrate, and an exchange coupling layer provided on the magnetic recording layer to add an action of exchange coupling the magnetic particles, and is characterized by having an ion irradiation step of performing ion irradiation on the entire surface of the exchange coupling layer after layering the exchange coupling layer on the magnetic recording layer.
1. A method of manufacturing a magnetic recording medium comprising:
providing a non-magnetic substrate;
forming a magnetic recording layer of a granular structure having nonmagnetic boundary portions between pillar-shaped magnetic particles on the nonmagnetic substrate;
layering an exchange coupling layer on the magnetic recording layer to add an action of exchange coupling the magnetic particles, said exchange coupling layer being a film containing a metal having a hexagonal close-packed structure and providing an exchange coupling layer surface; and
performing ion irradiation on the entire exchange coupling layer surface after layering the exchange coupling layer on the magnetic recording layer,
wherein an amount of change in a ratio c/a of a c-axis to an a-axis in a crystal lattice of the metal having the hexagonal close-packed structure contained in the exchange coupling layer is |0.2|% or more after performing said ion irradiation.
2. The method of manufacturing a magnetic recording medium according to claim 1 , wherein the exchange coupling layer is a film containing Pt and Co, and the metal is Co.
3. The method of manufacturing a magnetic recording medium according to claim 1 , wherein a thickness of the exchange coupling layer is 7 nm or less, and a dose in the ion irradiation is in the range of 1×10 13 to 1×10 15 (ions/cm 2 ).
4. The method of manufacturing a magnetic recording medium according to claim 1 , wherein in the ion irradiation step, ions are applied from above a protective layer after layering the exchange coupling layer on the magnetic recording layer and further forming the protective layer on the exchange coupling layer.
5. The method of manufacturing a magnetic recording medium according to claim 1 , wherein a thickness of the exchange coupling layer is 7 nm or less.
6. The method of manufacturing a magnetic recording medium according to claim 1 wherein a dose in the ion irradiation is in the range of 1×10 13 to 1×10 15 (ions/cm 2 ).