Polyolefin composition comprising crosslinkable polyolefin with silane groups, silanol condensation catalyst and silicon containing compound
View Patent ↗The present invention relates to a composition comprising (i) a crosslinkable polyolefin with hydrolysable silane groups (A), (ii) a silanol condensation catalyst (B) of the formula Ar(SO 3 H) x as defined herein, and (iii) a silicon containing compound (C) selected from the group consisting of 3-ureidopropyltrimethoxysilane, N-trimethoxysilylmethyl-O-methylcarbamate, and mixtures thereof; to an article, in particular a wire or cable, comprising such a composition, and to the use of such a composition for producing the article. The present invention further relates to the use of silicon containing compound (C) as a processing aid in the compounding of polyolefin compositions and as a surface smoothening agent in polyolefin compositions. Finally, the present invention relates to the use of a silicon containing compound (C) as a drying agent for polyolefin compositions, as a corrosion inhibitor in polyolefin compositions comprising a Bronsted acid and as a pH controlling agent in polymer compositions comprising a Bronsted acid.
1. Process for removing water during extrusion of a polyolefin composition, comprising:
adding a silicon containing compound (C) to the polyolefin composition during extrusion;
wherein the polyolefin composition comprises a crosslinkable polyolefin with hydrolysable silane groups (A) and a silanol condensation catalyst (B); and
wherein the silicon containing compound (C) is selected from the group consisting of Ureidopropyltrimethoxysilane, N-Trimethoxysilylmethyl-O-methylcarbamate, and mixtures thereof.
2. A method for removing water from a polyolefin composition during compounding, comprising:
adding a silicon containing compound (C) to the polyolefin composition during compounding of the polyolefin composition;
wherein the polyolefin composition comprises a crosslinkable polyolefin with hydrolysable silane groups (A) and a silanol condensation catalyst (B);
wherein the silicon containing compound (C) is selected from the group consisting of 3-Ureidopropyltrimethoxysilane, N-Trimethoxysilylmethyl-O-methylcarbamate, and mixtures thereof; and
wherein the silanol condensation catalyst (B) is an organic sulphonic acid comprising the structural element:
Ar(SO 3 H) x (II)
with Ar being an aryl group substituted with at least one C 4 - to C 30 -hydrocarbyl group and the total silanol condensation catalyst (B) comprises from 10 to 200 C-atoms and x being at least 1; and
wherein the silicon containing compound (C) is a drying agent and water is removed during compounding.
3. The method of claim 2 , wherein the crosslinkable polyolefin with hydrolysable silane groups (A) comprises a polyethylene with hydrolysable silane groups.