High-strength steel sheet with excellent low temperature toughness and manufacturing thereof
There is provided a high-strength steel plate having acicular ferrite and bainite as a main microstructure and an austenite/martensite (M & A) as a second phase under the control of a cooling rate above the austenite transformation temperature. The high-strength steel plate comprises: carbon (C): 0.03 to 0.10 wt %, silicon (Si): 0.1 to 0.4 wt %, manganese (Mn): 1.8 wt % or less, nickel (Ni): 1.0 wt % or less, titanium (Ti): 0.005 to 0.03 wt %, niobium (Nb): 0.02 to 0.10 wt %, aluminum (Al): 0.01 to 0.05 wt %, calcium (Ca): 0.006 wt % or less, nitrogen (N): 0.001 to 0.006 wt %, phosphorus (P): 0.02 wt % or less, sulfur (S): 0.005 wt % or less, and the balance of iron (Fe) and other inevitable impurities. The method for manufacturing a high-strength steel plate may be useful to economically and effectively manufacture a high strength steel, which is able to secure excellent properties such as high strength and high toughness since the acicular ferrite and bainite may be effectively formed without adding expensive elements such as molybdenum (Mo).
1. A high-strength steel plate, comprising: carbon (C): 0.03 to 0.10% by weight, silicon (Si): 0.1 to 0.4% by weight, manganese (Mn): 1.8 wt % or less, nickel (Ni): 1.0 wt % or less, titanium (Ti): 0.005 to 0.03 wt %, niobium (Nb): 0.02 to 0.10 wt %, aluminum (Al): 0.01 to 0.05 wt %, calcium (Ca): 0.006 wt % or less, nitrogen (N): 0.001 to 0.006 wt %, phosphorus (P): 0.02 wt % or less, sulfur (S): 0.005 wt % or less, and the balance of iron (Fe) and other inevitable impurities, wherein a microstructure of the steel plate comprises acicular ferrite and bainite as a main microstructure and an austenite/martensite (M&A) as a second phase, and wherein the acicular ferrite has a grain size of 10 μm (micrometers) or less (excluding 0), and the bainite has a packet size of 5 μm (micrometers) or less (excluding 0), wherein the microstructure of the steel comprises substantially no polygonal ferrite.
2. The high-strength steel plate of claim 1 , wherein the austenite/martensite (M&A) has an area fraction of 10% or less (excluding 0%).
3. The high-strength steel plate of claim 1 , wherein a yield strength of the high-strength steel plate is in a range of 500 to 650 MPa, and a Charpy impact-absorbed energy at −40° C. is 300 J or more.
4. The high-strength steel plate of claim 2 , wherein a yield strength of the high-strength steel plate is in a range of 500 to 650 MPa, and a Charpy impact-absorbed energy at −40° C. is 300 J or more.
5. The high-strength steel plate of claim 1 , wherein the acicular ferrite and bainite as the main microstructure has an area fraction of at least 90%.
6. The high-strength steel plate of claim 1 , wherein the acicular ferrite and bainite as the main microstructure has an area fraction of at least 92%.