Polyurethane dispersions and coatings produced therefrom
The present invention discloses polyurethane dispersions based on aliphatic isocyanates which form hard coatings wherein the coatings also have good solvent resistant properties. The enhanced properties of the coatings are achieved by including from 1 to 8 weight percent of a high functional polyol in the polyol formulation for producing the dispersions.
1. An aqueous polyurethane dispersion containing polyurethane solids and a non-aqueous, organic solvent content of less than 5 weight percent wherein the polyurethane solids are obtained from a polyurethane prepolymer prepared by reacting
a) a polyol comprising
ai) from 92 to 99 wt % of a polyol or polyol blend having a mean average equivalent weight of 150 to 600 and a nominal average functionality of from 1.5 to 2.9 and
aii) from 1 to 8 wt % of at least one polyol having a nominal functionality of 5 to 8; and an equivalent weight of 100 to 170;
(b) at least one aliphatic polyisocyanate;
(c) optionally additional stabilizers; and
(d) optionally chain extenders
wherein the prepolymer has an isocyanate (NCO) content of from 2 to 20 wt %, and wherein the solids content of the dispersion is from 30 to 60 weight percent.
2. The dispersion of claim 1 wherein the isocyanate is 1,6-hexamethylene-diisocyanate (HDI); isophorone diisocyanate (IPDI); 2,4- and 2,6-hexahydrotoluene-diisocyanate; 4,4′-, 2,2′- and 2,4′-dicyclohexylmethanediisocyanate (H12MDI); tetramethyl xylene diisocyanate, norbomane diisocyanate; 1,3- and 1,4-(bisisocyanatomethyl)cyclohexane (including cis- or trans-isomers thereof); tetramethylene-1,4-diisocyanate (TMXDI); cyclohexane 1,4-diisocyanate; 4,4′-dicyclohexylmethane diisocyanate; xylene diisocyanate; 1,12-dodecane diisocyanate; 2,2,4-trimethylhexamethaylene diisocyanate; or a mixture thereof.
3. The dispersion of claim 1 wherein polyol ai) has a mean average equivalent weight of 75 to 500.
4. The dispersion of claim 1 wherein the dispersion is made in a continuous process.
5. A hard coating on a surface comprising the polyurethane dispersion of claim 1 .
6. An isocyanate terminated prepolymer comprising
a) a polyol having
ai) from 92 to 99 wt % of a polyol or polyol blend having a mean average equivalent weight of 150 to 600 and a nominal average functionality of from 1.5 to 2.9; and
aii) from 1 to 8 wt % of at least one polyol having a nominal functionality of 5 to 8; and an equivalent weight of 100 to 170; and
(b) at least one aliphatic polyisocyanate;
wherein the prepolymer has a free isocyanate content of from 2 to 20 wt %.