Mix and refractory product having a high hydration resistance produced therefrom
View Patent ↗Mix which comprises a) one or more very finely divided silicon dioxide powders having an average particle diameter of from 2 to 100 nm and a BET surface area of at least 30 m 2 /g, b) one or more particulate components selected from the group consisting of oxides, carbides and nitrides, in each case having an average particle diameter of from >0.5 μm to 30 mm, c) one or more synthetic resins as binders and d) one or more metallic antioxidants having an average particle diameter of from >0.5 to 250 μm. Process for producing a shaped body, in which to the mix is introduced into a mould, pressed if appropriate and heated to a temperature at which the synthetic resin crosslinks thermally. Shaped body which can be obtained therefrom. Process for producing a refractory shaped body, in which the shaped body is carbonized. Refractory shaped body which can be obtained therefrom.
1. A mix, comprising
a) at least one very finely divided, aggregated, pyrogenic silicon dioxide powder having an average particle diameter of from 2 to 100 nm and a BET surface area of at least 30 m 2 /g, wherein the very finely divided, aggregated, pyrogenic silicon dioxide powder is in the form of an organic dispersion having a silicon dioxide content of at least 15 wt %,
b) magnesium oxide having an average particle diameter of from >0.5 μm to 30 mm,
c) at least one synthetic resin as binder, and
d) at least one metallic antioxidant having an average particle diameter of from >0.5 to 250 μm;
wherein the at least one very finely divided, aggregated, pyrogenic silicon dioxide powder is present in the mix in an amount of from 0.01 to 5 percent by mass, based on the magnesium oxide.
2. The mix according to claim 1 , further comprising at least one binder selected from the group consisting of synthetic pitch, pitch, bitumen and carbon.
3. The mix according to claim 1 , wherein the proportion of the at least one synthetic resin is from 0.5 to 20 per cent by mass, based on the magnesium content.
4. The mix according to claim 1 , wherein the at least one metallic antioxidant is at least one powder selected from the group consisting of aluminum, iron, magnesium, silicon, and titanium.
5. The mix according to claim 1 , wherein the proportion of the at least one metallic antioxidant is from 0.5 to 5 per cent by mass, based on magnesium oxide.
6. A process for producing a shaped body, comprising:
optionally, adding at least one hardener to the mix according to claim 1 ;
introducing the mix into a mold;
optionally, pressing; and
heating to a temperature at which the at least one synthetic resin crosslinks thermally.
7. The process according to claim 6 , wherein the shaped body is at least one slider plate, immersed discharge outlet, stopper, flushing cone, shadow tube, outlet nozzle, membrane, thermal insulation material, heat shield, graphite electrode, or refractory brick.
8. The mix according to claim 1 , wherein the organic dispersion comprises at least one selected from the group consisting of an alcohol and a diol.
9. The mix according to claim 1 , wherein the organic dispersion comprises ethylene glycol.