Red emitting SiAlON-based material
View Patent ↗The invention relates to a red emitting material of the composition a(M II N 2/3 )*b(M III N)*c(M IV N 4/3 )*d 1 CeO 3/2 *d 2 EuO*xM IV O2*yM III O 3/2 with Cerium and Europium present in the material. This material has been found to have an increased lumen equivalent and absorption efficiency of blue light.
1. Red emitting material essentially having a main phase of the composition
a (M II N 2/3 )* b (M III N)* c (M IV N 4/3 )* d 1 CeO 3/2 *d 2 EuO* x M IV O 2 *y M III O 3/2
wherein M II is an alkaline earth metal chosen of the group of Ca, Mg, Sr and Ba or mixtures thereof, M IV is selected out of the group comprising Si, Ge, C, Zr, Hf or mixtures thereof, and M III is selected out of the group comprising Al, B, Sc, Ga, and Lu or mixtures thereof,
with
0.95 *c≦a+d 1 +d 2 ≦1.2 *b and a+d 1 +d 2 ≧c+x,
( b+y ):( c+x )≧1,
( b+y )≦1+10 *d 1 ,
b≧ 5 *y,
c≧ 10 *x,
0.001≦ d 1 ≦0.01,
0.001≦ d 2 ≦0.005,
0≦( d 1 +d 2 +x+y )≦0.4.
2. The material of claim 1 , whereby d 2 *0.1≦d 1 ≦d 2 *10.
3. The material of claim 1 , having a lumen equivalent LE of ≧100 lm/W.
4. The material of claim 1 , essentially having a main phase of the composition
a (CaN 2/3 )* b (AlN)* c (SiN 4/3 )* d 1 CeO 3/2 *d 2 EuO* x SiO 2 *y AlO 3/2
with
0.95 *c≦a+d 1 +d 2 ≦1.2 *b and a+d 1 +d 2 c+x,
( b+y ):( c+x )≧1,
( b+y )≦1+10 *d 1 ,
b≧ 5* y,
c≧ 10* x,
0.001 ≦d 1 ≦0.01
0.001 ≦d 2 ≦0.005
d 1 ≦d 2
0.01 *d 2 ≦d 1 ≦10 *d 2
0≦( d 1 +d 2 +x+y )≦0.4.
5. A ceramic material comprising a red emitting material according to claim 1 .
6. The ceramic material of claim 5 , whereby the photothermal stability of the ceramic material is ≧80% to ≦100% after exposure of the ceramic material for 1000 hrs at 200° C. with a light power density of 10 W/cm 2 and an average photon energy of 2.75 eV.
7. The ceramic material of claim 5 , whereby the thermal conductivity of the ceramic material at room temperature is ≧2 W cm −1 K −1 to ≦70 W cm −1 K −1 .
8. The ceramic material of claim 5 , whereby the ceramic material has a density of ≧95% and ≦101% of the theoretical density.
9. A light emitting device, especially a LED, comprising a ceramic material according to claim 5 , which comprises a red emitting material essentially having a main phase of the composition
a (M II N 2/3 )* b (M III N)* c (M IV N 4/3 )* d 1 CeO 3/2 *d 2 EuO* x M IV O 2 *y M III O 3/2
wherein M II is an alkaline earth metal chosen of the group of Ca, Mg, Sr and Ba or mixtures thereof, M IV is selected out of the group comprising Si, Ge, C, Zr, Hf or mixtures thereof, and M III is selected out of the group comprising Al, B, Sc, Ga, and Lu or mixtures thereof, with
0.95 *c≦a+d 1 +d 2 ≦1.2 *b and a+d 1 +d 2 ≧c+x,
( b+y ):( c+x )≧1,
( b+y )≦1+10 *d 1 ,
b≧ 5* y,
c≧ 10* x,
d 1 >0
d 2 ≧0.001.
10. A system comprising a material and/or ceramic material according to claim 1 , the system being used in one or more of the following applications: Office lighting systems household application systems shop lighting systems, home lighting systems, accent lighting systems, spot lighting systems, theater lighting systems, fiber-optics application systems, projection systems, self-lit display systems, pixelated display systems, segmented display systems, warning sign systems, medical lighting application systems, indicator sign systems, and decorative lighting systems portable systems automotive applications green house lighting systems.