Doped positive electrode active materials and lithium ion secondary battery constructed therefrom
View Patent ↗Positive electrode active materials comprising a dopant in an amount of 0.1 to 10 mole percent of Mg, Ca, Sr, Ba, Zn, Cd or a combination thereof are described that have high specific discharge capacity upon cycling at room temperature and at a moderate discharge rate. Some materials of interest have the formula Li 1+x Ni α Mn β-δ Co γ A δ X μ O 2−z F z , where x ranges from about 0.01 to about 0.3, δ ranges from about 0.001 to about 0.15, and the sum x+α+β+γ+δ+μ can approximately equal 1.0. The materials can be coated with a metal fluoride to improve the performance of the materials especially upon cycling. The materials generally can have a tap density of at least 1.8 g/mL. Also, the materials can have an average discharge voltage of around 3.6 V.
1. A positive electrode active material comprising a layered composite crystalline active composition with a formula Li 1+x Ni α Mn β-δ Co γ A δ X μ O 2 ,
wherein x ranges from about 0.01 to about 0.3,
α ranges from about 0.1 to about 0.4,
β ranges from about 0.25 to about 0.65,
γ ranges from 0.075 to about 0.4,
δ ranges from about 0.01 to about 0.035,
μ ranges from 0 to about 0.1, and
wherein A is Mg, Ca, Sr, Ba, Zn, Cd, or combinations thereof and X is a transition metal or a combination thereof other than A, Ni, Mn and Co, and
a stabilization coating over the active composition,
wherein the material has a 10th cycle specific discharge capacity of at least about 240 mAh/g at a discharge rate of C/3 when discharged from 4.6 volts to 2.0 volts and wherein the 40th cycle specific discharge capacity is at least about 98% of the 10th cycle specific discharge capacity at room temperature at a discharge rate of C/3 and from 4.6 volts to 2.0 volts.
2. The positive electrode active material of claim 1 wherein the sum x+α+β+γ+δ+μ approximately equals 1.0.
3. The positive electrode active material of claim 1 wherein A is magnesium,
x ranges from about 0.175 to about 0.225,
α ranges from about 0.150 to about 0.2,
β ranges from about 0.52 to about 0.57,
γ ranges from about 0.075 to about 0.125, and
δ ranges from about 0.01 to about 0.030.
4. The positive electrode active material of claim 1 wherein the stabilization coating is a metal fluoride coating in an amount from about 3 nm to about 11 nm.
5. The positive electrode active material of claim 4 wherein the metal fluoride comprises AlF 3 .
6. The positive electrode active material of claim 1 wherein the material has a 10th cycle discharge capacity from about 250 mAh/g to about 270 mAh/g at room temperature at a discharge rate of C/3 when discharged from 4.6 volts to 2.0 volts.
7. The positive electrode active material of claim 1 having a tap density of at least about 1.8 g/mL.
8. The positive electrode active material of claim 1 having a first cycle irreversible capacity loss of no more than about 70 mAh/g at a discharge rate of C/10.
9. A positive electrode comprising the positive electrode active material of claim 1 , an electrically conductive material that is distinct from the positive electrode active material, and a binder.
10. The positive electrode active material of claim 1 having:
an average discharge voltage of at least about 3.63 volts at a discharge rate of C/10.
11. The positive electrode active material of claim 1 wherein A is Mg.
12. The positive electrode active material of claim 10 wherein the material comprises from about 3 nm to about 11 nm metal fluoride coating.
13. The positive electrode active material of claim 10 wherein the material has a 10th cycle discharge capacity from about 250 mAh/g to about 270 mAh/g at room temperature at a discharge rate of C/3 when discharged from 4.6 volts to 2.0 volts.
14. The positive electrode active material of claim 10 having a tap density of at least about 1.8 g/mL.
15. A lithium ion secondary battery comprising a positive electrode comprising the positive electrode active material of claim 1 , a negative electrode comprising elemental carbon and a separator between the positive electrode and the negative electrode.
16. A method for the synthesis of a layered lithium metal oxide composition of claim 1 , the method comprising precipitating a mixed metal hydroxide or carbonate composition from a solution comprising +2 metal cations, wherein the mixed metal hydroxide or carbonate composition has a selected stoichiometry comprising Ni +2 , Mn +2 , Co +2 with a dopant concentration from about 0.1 to about 10 mole percent wherein the dopant comprises Mg, Ca, Sr, Ba, Zn, Cd or a combination thereof.
17. The method of claim 16 further comprising the addition of a lithium source in powder form to the metal hydroxide or carbonate composition to form a mixture and heating the mixture to form a corresponding crystalline lithium metal oxide particles.
18. The positive electrode active material of claim 1 for a lithium ion battery having:
an average discharge voltage of at least about 3.63 volts at a discharge rate of C/10, and
a 46th cycle discharge capacity of at least about 170 mAh/g at room temperature at a discharge rate of 2C and from 4.6 volts to 2.0 volts.