Composite precursor for aluminum-containing lithium transition metal oxide and process for preparation of the same
View Patent ↗The present invention provides a powdery composite precursor, which comprises a core of a lithium transition metal oxide, and an aluminum hydroxide-based precipitate layer coated on the surface of the core, and a process to prepare the composite precursor. The preparation process comprises the formation of a water based slurry by dispersing lithium transition metal oxide powder in water, and a precipitation reaction of an aluminum salt solution with a base solution where the lithium transition metal particles act as seed particles, whereby a mechanically stable precipitate layer of homogeneous thickness can be achieved. The composite precursor can be converted into aluminum-containing, e.g., aluminum-doped, lithium transition metal oxide suitable for a cathode active material of lithium rechargeable battery by heat treatment.
1. A composite precursor for an aluminum-containing lithium transition metal oxide, the composite precursor comprising:
(a) a lithium transition metal oxide core, and
(b) an aluminum hydroxide-based precipitate layer comprising an active aluminum phase on a surface of the lithium transition metal oxide core,
wherein the aluminum hydroxide-based precipitate layer comprises a divalent anion,
the divalent anion is sulfate, and
the aluminum hydroxide-based precipitate layer comprises a lithium-aluminum-sulfate -hydroxide-hydrate.
2. The composite precursor according to claim 1 , wherein the total amount of aluminum in the precipitate layer is 0.5 to 5 atomic percent, based on the total amount of transition metal in the composite precursor.
3. The composite precursor according to claim 1 , wherein the lithium transition metal oxide as the core of composite precursor has a layered or spinel crystal structure.
4. The composite precursor according to claim 3 , wherein the lithium. transition metal oxide as the core of composite precursor is one or more selected from the group consisting of LiCoO 2 , cobalt-rich Li(Mn 1/2 Ni 1/2 ) 1-x Co x O 2 (0.5<x<1), lithium manganese spinel, lithium manganese-nickel spinel, lithium manganese nickel oxide, and lithium nickel oxide- based materials.
5. The composite precursor according to claim 4 , wherein the lithium transition metal oxide as the core of composite precursor i.s one or more selected from the group consisting of LiCoO 2 , cobalt-rich Li(Mn 1/2 Ni 1/2 ) 1-x Co x O 2 (0.5<x<1), lithium manganese spinel, and lithium manganese-nickel spinel.
6. The composite precursor according to claim 5 , wherein the lithium transition metal oxide as the core of composite precursor is LiCoO 2 or lithium manganese spinel.
7. A process for preparation of the composite precursor according to claim 1 , comprising a step of carrying out a precipitation reaction of an aluminum salt solution and a base salt solution with a lithium transition metal oxide as seed particles dispersed in a water-based shiny or paste to form the aluminum hydroxide-based precipitate layer on the surface of the lithium transition metal oxide core to prepare the composite precursor,
wherein the aluminum salt solution comprises one or more selected from the group consisting of aluminum sulfate, sodium aluminum sulfate, and potassium aluminum sulfate, and
wherein the base salt solution comprises one or more selected from the group consisting of lithium hydroxide, sodium hydroxide, ammonium hydroxide, and potassium hydroxide.
8. The process according to claim 7 , wherein the lithium transition metal oxide as a raw material is tolerated to contain impurities of sulfur, sodium or chloride.
9. The process according to claim 7 , wherein the aluminum salt is aluminum sulfate.
10. The process according to claim 7 , wherein the aluminum salt is used in combination with cobalt and/or nickel sulfate.
11. The process according to claim 7 , wherein the base salt is lithium hydroxide.
12. The process according to claim 7 , wherein after the precipitation reaction, the coated particle is separated and/or washed, followed by drying.
13. The process according to claim 12 , wherein before or after drying, LiPO 3 is further added in an aqueous form.
14. The process according to claim 12 , wherein after drying, Li 3 AlF 6 is mixed in a solid, powder form.
15. An aluminum-containing lithium transition metal oxide for a cathode active material of lithium rechargeable battery, produced by heating the composite precursor of claim 1 in the range of 500˜1050° C.
16. The aluminum-containing lithium transition metal oxide according to claim 15 , wherein the temperature of heat treatment is 750˜950° C.