Process for producing a body provided with a slot as a test crack
View Patent ↗A process for producing a reference body ( 10 ) provided with a slot ( 17 ) as a test crack for the nondestructive testing of materials can be used flexibly and includes the following steps: a) a reference body ( 10 ) and a mask ( 11 ) provided with a slot pattern ( 12 ) are provided; b) the mask ( 11 ) is applied to the reference body ( 10 ); c) material is removed from the reference body ( 10 ) through the mask ( 11 ) with an abrasive water jet ( 16 ); and d) the mask ( 11 ) is taken off the reference body ( 10 ).
1. A process for producing a reference body with a slot as a test crack for the nondestructive testing of materials, the process comprising:
providing a reference body and a mask having a slot pattern with a sub-millimeter width; applying the mask to the reference body;
removing material from the reference body through the mask with an abrasive water jet that consists of a pressurized abrasive suspension to form the slot having a predefined slot depth; including removing material with the abrasive water jet from a nozzle of a water jet apparatus having a diameter of 0.5 mm to 1.0 mm, and with a water jet with a pressure of 120 bar to 200 bar;
stop removing material after a predefined machining time and removing the water jet apparatus; and
removing the mask from the reference body.
2. The process as claimed in claim 1 , wherein providing the mask comprises providing a mask formed of a material which is more resistant to the abrasive water jet than the material of the reference body.
3. The process as claimed in claim 2 , wherein providing the mask comprises providing a mask formed of a hard metal.
4. The process as claimed in claim 2 , wherein providing the mask comprises providing a mask formed of tungsten carbide or a hard ceramic.
5. The process as claimed in claim 1 , wherein providing the mask comprises providing a mask in the form of a thin plate.
6. The process as claimed in claim 1 , wherein providing the mask comprises providing a magnetic mask or an adhesive on an underside of the mask so that the mask can be fastened on the reference body.
7. The process as claimed in claim 1 , wherein removing material comprises removing with a mixture of water and a fine-grain abrasive additive as the abrasive water jet.
8. The process as claimed in claim 7 , wherein the additive is an oxide ceramic or a garnet.
9. The process as claimed in claim 7 , wherein the mean grain size of the additive is 1 micrometer or less.
10. A process for producing a reference body and calibrating a testing apparatus, the process comprising:
producing the reference body with a slot as a test crack with a process including:
providing a reference body and a mask having a slot pattern with a sub-millimeter width; applying the mask to the reference body,
removing material from the reference body through the mask with an abrasive water jet that consists of a pressurized abrasive suspension to form the slot having a predefined slot depth; including removing material with the abrasive water jet from a nozzle of a water jet apparatus having a diameter of 0.5 mm to 1.0 mm, and with a water jet with a pressure of 120 bar to 200 bar;
stop removing material after a predefined machining time and removing the water jet apparatus; and
removing the mask from the reference body; and
calibrating the testing apparatus, testing processes, or both with the reference body test crack, wherein the testing processes comprise ultrasound processes.