Two-component waterborne polyurethane coatings
View Patent ↗A polyaziridine introduced into a two-component waterborne polyurethane dispersion coating system increases the cure rate of a coating composition formed from the coating system.
1. A process for increasing the cure rate of a two-component waterborne polyurethane dispersion coating, comprising:
introducing a polyaziridine into a coating system comprising:
a hydrophilically-modified water-dispersible polyisocyanate;
a polyol dispersed in water, optionally, in the presence of one or more organic solvents; and optionally, one or more additives or auxiliary agents; wherein the quantity of polyaziridine introduced comprises 0.42 to 0.85 percent by weight of the coating system and the introduction of the polyaziridine decreases the time-to-cure by at least 35 percent.
2. The process of claim 1 , wherein the introduction of the polyaziridine decreases the time-to-cure by at least 90 percent.
3. The process of claim 1 , wherein the polyaziridine comprises one or more tris-aziridinoproprionate derivatives selected from the group consisting of trimethylolpropane tris-(1-(2-methyl)aziridino)propionate, trimethylolpropane tris-3-(1-aziridinopropionate), pentaerythritol tris-3-(1-aziridinopropionate), and combinations of any thereof.
4. The process of claim 1 , wherein:
the polyisocyanate comprises at least one isocyanurate trimer based on hexamethylene diisocyanate and having at least one 3-(cyclohexyl-amino)-1-propanesulfonic acid or 3-(cyclohexyl-amino)-1-propanesulfonate group covalently linked to the isocyanurate through a urea bond; and
the polyol comprises a polyacrylic polyol.
5. The process of claim 1 , wherein the polyaziridine is introduced into the coating system by mixing with the polyol before introducing the polyisocyanate.
6. The process of claim 1 , wherein the polyaziridine is introduced into the coating system by mixing with the polyisocyanate before introducing the polyol.
7. The process of claim 1 , wherein the polyaziridine is introduced into the coating system by mixing after the polyisocyanate and the polyol are mixed.
8. A two-component waterborne polyurethane dispersion coating system comprising:
a hydrophilically-modified water-dispersible polyisocyanate; a polyol dispersed in water, optionally, in the presence of one or more organic solvents;
a polyaziddine in the quantity of 0.42 to 0.85 percent by weight of the coating system; and optionally, one or more additives or auxiliary agents;
wherein a time-to-cure of the coating system is decreased by at least 35 percent.
9. The coating system of claim 8 , wherein the quantity of polyaziridine is 0.65 to 0.85 percent by weight of the coating system.
10. The coating system of claim 8 , wherein the time-to-cure is decreased by at least 90 percent.
11. The coating system of claim 8 , wherein the polyaziridine comprises one or more tris-aziridinoproprionate derivatives selected from the group consisting of trimethylolpropane tris-(1-(2-methyl)aziridino)propionate, trimethylolpropane tris-3-(1-aziridinopropionate), pentaerythritol tris-3-(1-aziridinopropionate), and combinations of any thereof.
12. The coating system of claim 8 , wherein:
the polyisocyanate comprises at least one isocyanurate trimer based on hexamethylene diisocyanate and having at least one 3-(cyclohexyl-amino)-1-propanesulfonic acid or 3-(cyclohexyl-amino)-1-propanesulfonate group covalently linked to the isocyanurate through a urea bond; and the polyol comprises a polyacrylic polyol.
13. A process for preparing a coating composition from the coating system of claim 8 , comprising mixing the polyaziridine with the polyol and any auxiliary agents or additives, and then mixing in the polyisocyanate to form the coating composition.
14. A process for preparing a coating composition from the coating system of claim 8 , comprising mixing the polyaziridine with the polyisocyanate, and then mixing the combined polyaziridine and polyisocyanate with a mixture comprising the polyol and any auxiliary agents or additives to form the coating composition.
15. A process for preparing a coating composition from the coating system of claim 8 , comprising mixing the polyol, any auxiliary agents or additives, and the polyisocyanate to form the coating composition, and then mixing the polyaziridine into the coating composition.
16. A coating composition prepared from the coating system of claim 8 .
17. A substrate coated with a coating composition prepared from the coating system of claim 8 .
18. The process of claim 1 , wherein the quantity of polyaziridine introduced comprises 0.65 to 0.85 percent by weight of the coating system.