Wax blends for use with engineered wood composites
View Patent ↗Wax is a key ingredient in engineered wood composites, such as oriented strand board (OSB) and oriented strand lumber (OSL), to prevent and reduce swelling caused by water uptake. Wax, normally a byproduct of oil refining and lube production, is now considered a precious feedstock for producing higher margin product such as fuel or diesel. Disclosed herein are suitable alternative waxes to petroleum wax for use as sizing agents in producing engineered wood composites.
1. An engineered wood composite comprising at least one layer of wood flakes, wherein the wood flakes are bonded together by a binder resin and sized by a sizing agent, wherein the sizing agent comprises an effective blend of an effective ratio of a petroleum slack wax and a biowax, wherein the biowax is a wax substantially produced from a lipid derived from an animal or a plant, and wherein the petroleum slack wax has a melting point less than about 77° C. (170° F.), an oil content of about 5 wt % to about 30 wt %, and a flash point less than 316° C. (600° F.).
2. The engineered wood composite of claim 1 , wherein the biowax is produced from vegetable fat or vegetable oil.
3. The engineered wood composite of claim 1 , wherein the biowax comprises hydrogenated soybean, hydrogenated castor oil, or a combination thereof.
4. The engineered wood composite of claim 1 , wherein the biowax comprises tallow, hydrogenated tallow, tallow blended with hydrogenated tallow, or a combination thereof.
5. The engineered wood composite of claim 1 , wherein the melting of the petroleum slack wax is about 46° C. (115° F.) to about 77° C. (170° F.), wherein the oil content of the petroleum slack wax is about 5% to about 30%, and wherein the flash point of the petroleum slack wax is about 204° C. (400° F.) to about 316° C. (600° F.).
6. The engineered wood composite of claim 1 , wherein the biowax and the petroleum slack wax are blended at a wt % ratio of about 20:80 to about 80:20.
7. The engineered wood composite of claim 1 , wherein the biowax and the petroleum slack wax are blended at a wt % ratio of about 50:50.
8. The engineered wood composite of claim 1 , wherein the engineered wood composite is an oriented strand board, particle board, plywood, waferboard, chipboard, medium-density fiberboard, parallel strand lumber, oriented strand lumber, or laminated strand lumber.
9. The engineered wood composite of claim 1 , wherein the engineered wood composite is a panel.
10. The engineered wood composite of claim 1 wherein the measured edge swell is essentially equal to or less than the measured edge swell of an engineered wood composite comprising a sizing agent consisting essentially of petroleum wax.
11. An article comprising an engineered wood composite of claim 1 .
12. The article of claim 11 , wherein the article is a floor, wall, or roof.
13. A sizing agent composition, comprising a blend of a petroleum slack wax and a biowax, wherein the biowax is a wax substantially produced from a lipid derived from an animal or a plant, and wherein the petroleum slack wax has a melting point less than 77° C. (170° F.), an oil content of about 5% to about 30%, and a flash point less than 316° C. (600° F.).
14. The sizing agent composition of claim 13 , wherein the biowax comprises hydrogenated soybean or hydrogenated castor oil.
15. The sizing agent composition of claim 13 , wherein the biowax comprises tallow, hydrogenated tallow, tallow blended with hydrogenated tallow, or a combination thereof.
16. The sizing agent composition of claim 13 , further comprising one or more anti-oxidants, corrosion inhibitors, dyes, fungicides, insecticides, or any combination thereof.
17. A method of manufacturing an engineered wood composite, comprising:
coating a plurality of wood flakes with a binder resin and a sizing agent, wherein the sizing agent comprises a blend of a petroleum slack wax and a biowax, wherein the biowax is a wax substantially produced from a lipid derived from an animal or a plant, and wherein the petroleum slack wax has a melting point less than 77° C. (170° F.), an oil content of about 5% to about 30%, and a flash point less than 316° C. (600° F.);
assembling the coated flakes into a mat; and
curing the coated flakes in the mat to form the engineered wood composite.
18. The method of claim 17 , wherein the biowax is produced from animal fat, vegetable fat, or vegetable oil.
19. The method of claim 17 , wherein the biowax produced from vegetable fat, vegetable oil, hydrogenated soybean oil, hydrogenated castor oil, tallow, hydrogenated tallow, tallow blended with hydrogenated tallow, or a combination thereof.