Glass ceramics with bulk scattering properties and methods of making them
Described herein are glass ceramic compositions with bulk scattering properties that have improved light extraction properties due to high levels of diffuse transmission, and methods of making such glass ceramic compositions. The compositions are based on Li 2 O—Al 2 O 3 —SiO 2 glass ceramics and with the proper crystal size, exhibit good volume scattering characteristic for visible light and enhance the outcoupling from the substrate to the air in optical devices, such as light emitting diodes.
1. A glass ceramic comprising:
a composition comprising, in weight percent;
1.9-2.5% Li 2 O;
18-24% Al 2 O 3 ;
62-82% SiO 2 ; and
1-1.5% SnO 2 ;
wherein the glass ceramic is essentially free of TiO 2 , and exhibits diffuse transmission greater than or equal to 20% from 400 nm to 1200 nm; and
wherein the glass ceramic is colorless, essentially free of TiO 2 , and exhibits diffuse transmission greater than or equal to 20% from 400 nm to 1200 nm; and
wherein the glass ceramic is a bulk crystallized glass ceramic comprising crystals wherein the crystals have an average size from about 100 nm to about 2 μm and an average spacing of about 1 to 5 μm.
2. The glass ceramic of claim 1 having greater than 65% diffuse transmission from 400 nm to 700 nm.
3. The glass ceramic of claim 1 having greater than 60% total transmission from 400 nm to 700 nm.
4. The glass ceramic of claim 1 having greater than 60% diffuse transmission from 400 nm to 1200 nm.
5. The glass ceramic of claim 1 having greater than 80% total transmission from 400 nm to 1200 nm.
6. The glass ceramic of claim 1 ,
wherein the glass ceramic comprises 5-60 percent crystallization.
7. The glass ceramic of claim 1 , wherein the glass ceramic is essentially free of arsenic and fluorine.
8. A process for making a glass ceramic comprising:
preparing a glass wherein the composition comprises, in weight percent:
1.9-2.5% Li 2 O;
18-24% Al 2 O 3 ;
62-82% SiO 2 ;
1-1.5% SiO 2 ; and
wherein the glass is essentially free of TiO 2 and exhibits diffuse transmission greater than or equal to 20% from 400 nm to 1200 nm; and
thermally treating the glass to nucleate and grow crystals and form the glass ceramic, wherein the crystals have an average size from about 100 nm to about 2 μm and an average spacing of about 1 to 5 μm.
9. The process of claim 8 , which comprises heating the glass in a temperature range of 680° C. to 800° C. for at least a period of 15 minutes to nucleate the crystals.
10. The process of claim 8 , which comprises heating the glass in a temperature range of 880° C. to 950° C. for at least a period of 15 minutes to grow the crystals.
11. An OLED device comprising the glass ceramic of claim 1 .