High melt flow block copolymers for non-woven adhesives
View Patent ↗The present invention provides a low viscosity block copolymer for non-wovens construction adhesives of the formula [A−(A/B)]nX, wherein A represents an aromatic vinyl compound and (A/B) represents a polymer block obtained by random copolymerization of a mixture of a aromatic vinyl compound and butadiene in a weight ratio in the range of from 2:98 to 30:70, wherein n is an integer in the range of from 1 to 5, and wherein X is the remainder of the coupling agent.
1. A non-woven assembly adhesive comprising:
from about 20 to about 30 wt. % of styrenic block copolymer,
from about 40 to about 70 wt. % of tackifier resin, and
from about 5 to about 40 wt. % of plasticizer, all based on 100 wt % of the non-woven assembly adhesive,
said styrenic block copolymer having the formula of (S−S/B) n X, wherein S represents a polymer block of styrene and S/B represents a polymer block obtained by random copolymerization of a mixture of styrene and butadiene in a weight ratio in the range of from 2:98 to 30:70, and said styrenic block copolymer has a total apparent molecular weight from 20,000 to 150,000 g/mol, wherein n is an integer in the range of from 1 to 5, wherein X is the remainder of the coupling agent; and said styrenic block copolymer has a melt flow rate ranging from 40 to about 60 g/min., at 200° C./5 kg;
said tackifier is selected from C5-C9 hydrocarbon resin; and
said plasticizer is an oil compatible with said styrenic block copolymer and said tackifier resin.
2. The non-woven assembly adhesive of claim 1 , wherein said styrenic block copolymer has a coupling efficiency of 70 to about 98%.
3. The non-woven assembly adhesive of claim 1 , wherein said S/B block has a vinyl content in the range of about 7 to about 15 wt. %.
4. The non-woven assembly adhesive of claim 1 , wherein said S/B has average homopolymer block lengths of less than 100 monomer units.
5. The non-woven assembly adhesive of claim 4 , wherein said S/B has average homopolymer block lengths of less than 20 monomer units.
6. The non-woven assembly adhesive of claim 1 , wherein said styrenic block copolymer comprises a polystyrene end-block content from about 30 to about 60 wt. %.
7. A non-woven assembly, comprising a non-woven layer and an adhesive secured thereto, said adhesive comprising
from about 20 to about 30 wt. % of styrenic block copolymer,
from about 40 to about 70 wt. % of tackifier resin, and
from about 5 to about 40 wt. % of plasticizer, all based on 100 wt % of the non-woven assembly adhesive,
said styrenic block copolymer having the formula of (S−S/B) n X, wherein S represents a polymer block of styrene and S/B represents a polymer block obtained by random copolymerization of a mixture of styrene and butadiene in a weight ratio in the range of from 2:98 to 30:70, and said styrenic block copolymer has a total apparent molecular weight from 20,000 to 150,000 g/mol, wherein n is an integer in the range of from 1 to 5, wherein X is the remainder of the coupling agent; and said styrenic block copolymer has a melt flow rate ranging from 40 to about 60 g/min., at 200° C./5 kg;
said tackifier is selected from C5-C9 hydrocarbon resin; and
said plasticizer is an oil compatible with said styrenic block copolymer and said tackifier resin.
8. The non-woven assembly of claim 7 , wherein said styrenic block copolymer has a coupling efficiency of 70 to about 98%.
9. The non-woven assembly of claim 7 , wherein said S/B block has a vinyl content in the range of about 7 to about 15 wt. %.
10. The non-woven assembly of claim 7 , wherein said assembly is a diaper, personal sanitary articles, or a bed pad.
11. The non-woven assembly of claim 7 , wherein said styrenic block copolymer comprises a polystyrene end-block content from about 30 to about 60 wt. %.
12. The non-woven assembly of claim 7 , wherein said S/B has average homopolymer block lengths of less than 100 monomer units.