Nanostructured materials for battery applications
View Patent ↗The present invention relates to nanostructured materials (including nanowires) for use in batteries. Exemplary materials include carbon-comprising, Si-based nanostructures, nanostructured materials disposed on carbon-based substrates, and nanostructures comprising nanoscale scaffolds. The present invention also provides methods of preparing battery electrodes, and batteries, using the nanostructured materials.
1. A battery slurry, comprising:
a mixture of graphite, carbon, a polymer binder and an additive;
the additive comprising substantially homogeneous Si-based nanowires and graphite powder,
wherein the Si-based nanowires have a diameter of about 20 nm to about 100 nm and a length of about 0.1 microns to 50 microns, the nanowires being grown directly on and attached to the surface of the graphite powder and having a core-shell structure;
wherein the graphite powder is in the form of separate particles having diameter of about 5 microns to about 50 microns; and
wherein the weight % ratio of the additive in the battery slurry is between 1% and 80%.
2. The battery slurry of claim 1 , wherein the additive is about 10 weight % of the slurry.
3. A battery anode electrode, comprising:
a current collector; and
a coating layer formed on the current collector, the coating layer comprising a slurry comprising a mixture of graphite, carbon, a polymer binder, and an additive,
the additive comprising substantially homogeneous Si-based nanowires and graphite powder,
wherein the Si-based nanowires have a diameter of about 20 nm to about 100 nm and a length of about 0.1 microns to 50 microns, the nanowires being grown directly on and attached to the surface of the graphite powder and having a core-shell structure;
wherein the graphite powder is in the form of separate particles having diameter of about 5 microns to about 50 microns, and
wherein the weight % ratio of the additive in the battery slurry is between 1% and 80%.
4. The battery anode electrode of claim 3 , wherein the Si-based nanowires comprise Li inserted in the nanowires.
5. A battery, comprising:
the battery anode electrode according to claim 3 ;
a cathode; and
a separator positioned between the battery anode electrode and the cathode.
6. The battery of claim 5 , wherein the battery is a Li-ion battery.
7. The battery of claim 5 , wherein the cathode comprises LiCoO 2 , LiFePO 4 , LiMnO 2 , LiMnO 4 , LiNiCoAlO/LiNiCoMnO + LiMn 2 O 4 , LiCoFePO 4 or LiNiO 2 .
8. The battery of claim 5 , further comprising a housing encasing the anode, the separator and the cathode.
9. A method of making a battery anode electrode comprising the steps of:
(a) providing an additive comprising a plurality of substantially homogeneous Si-based nanowires and graphite powder, wherein the Si-based nanowires have a core-shell structure and are grown directly on and attached to the surface of the graphite powder and wherein the graphite powder is in the form of separate particles having a diameter of about 5 microns to about 50 microns;
(b) mixing the additive with graphite, carbon, solvent and a polymer binder to form a slurry, the weight % ratio of the additive in the slurry being between 1% and 80%; and
(c) forming the slurry into a battery anode electrode.
10. The method of claim 9 , wherein the providing comprises providing Si-based nanowires that have a diameter of about 20 nm to about 200 nm, and a length of about 0.1 microns to about 50 microns.
11. The method of claim 9 , wherein the forming step comprises:
coating the slurry onto a current collector;
drying the slurry in a coater dryer; and
recovering the solvent in a solvent recovery mechanism.
12. The method of claim 9 , further comprising:
after the providing step (a) and before the mixing step (b), disposing a carbon-comprising polymer on the Si-based nanowires and heating the carbon-comprising polymer at a temperature between 160° C. and 1000° C. to form a carbon coating on the Si-based nanowires.
13. The battery slurry of claim 1 , wherein the core comprises Si and the shell comprises amorphous C.
14. The battery slurry of claim 1 , wherein the core comprises crystalline Si, and the shell comprises amorphous Si.
15. The battery slurry of claim 1 , wherein the slurry further comprises a carbon coating disposed on the Si-based nanowires.
16. The battery slurry of claim 1 , wherein the Si-based nanowires comprise nanoparticles disposed on the surface of the Si-based nanowires.
17. The battery slurry of claim 16 , wherein the nanoparticles comprise graphene nanoparticles, graphite nanoparticles, Si nanoparticles or TiO 2 .
18. The battery slurry of claim 16 , wherein the nanoparticles comprise graphene layers or graphite layers.
19. A method of preparing a slurry for a battery anode electrode, comprising the step of:
(a) providing an additive comprising a plurality of substantially homogeneous Si-based nanowires and graphite powder, wherein the Si-based nanowires have a core-shell structure, the Si-based nanowires being grown directly on and attached to the surface of the graphite powder and the Si-based nanowires having a diameter between 20 nm and 100 nm and a length between 0.1 microns to 50 microns and wherein the graphite powder is in the form of separate particles having diameter of about 5 microns to about 50 microns;
(b) mixing the additive with graphite, carbon, solvent and a polymer binder to form a slurry, the weight % ration of the additive in the slurry being between 1% and 80%.
20. A method according to claim 19 , further comprising: after the providing step (a) and before the mixing step (b), disposing a carbon coating on the Si-based nanowire.
21. A method according to claim 19 , further comprising: after the providing step (a) and before the mixing step (b), disposing a carbon comprising polymer on the Si-based nanowires and heating the carbon-comprising polymer to form a carbon coating on the Si-based nanowires.