Ethylene polymerization catalysts
View Patent ↗The present invention relates to solid catalyst components comprising a reaction product of a titanium compound, a magnesium compound, an alcohol, an aluminum alkoxide, a siloxane mixture, and a maleate derivative; and catalyst systems comprising the solid catalyst components and organoaluminum compounds. The present invention also relates to methods of making the solid catalyst components and the catalyst systems, and methods of polymerizing or copolymerizing ethylene using the catalyst systems.
1. A process of producing a solid catalyst component for use in ethylene polymerization, the process comprising:
adding a magnesium compound, an aluminum alkoxide, and a first amount of a siloxane mixture into an alcohol solution to form a mixture;
heating the mixture to form a magnesium solution;
contacting the magnesium solution with a titanium compound;
adding an additional amount of the siloxane mixture to form a liquid catalyst intermediate;
heating the liquid catalyst intermediate to form catalyst intermediate particles; and
contacting the catalyst intermediate particles with a maleate derivative to form the solid catalyst component.
2. The process according to claim 1 , wherein the titanium compound has a general formula: TiX n (OR) 4-n , wherein R is a hydrocarbon radical having 1 to 20 carbon atoms, X is a halogen, and n is from 1 to 4.
3. The process according to claim 1 , wherein the magnesium compound is a magnesium halide, an alkoxy magnesium halide, an aryloxy magnesium halide, aryloxy magnesium, or a carboxylic acid salt of magnesium.
4. The process according to claim 1 , wherein the alcohol solution comprises an alcohol species that contains 8 to 20 carbon atoms.
5. The process according to claim 1 , wherein the maleate derivative has a general formula (I):
wherein R 1 and R 2 are the same or different, and wherein each of R 1 and R 2 is represented by a C 2 -C 20 linear alkyl radical, a C 2 -C 20 branched alkyl radical, or a C 7 -C 20 alkylaryl radical.
6. The process according to claim 5 , wherein the maleate derivative is a dialkyl maleate.
7. The process according to claim 6 , wherein the dialkyl maleate comprises at least one selected from the group consisting of diethyl maleate, din-propyl maleate, di-iso-propyl maleate, di-n-butyl maleate, di-iso-butyl maleate, di-n-pentyl maleate, di-iso-pentyl maleate, dineopentyl maleate, di-n-hexyl maleate, di-iso-hexyl maleate, di-n-heptyl maleate, di-iso-heptyl maleate, di-n-octyl maleate, bis(2,2-dimethylhexyl) maleate, bis(2-ethylhexyl) maleate, di-n-nonyl maleate, diisodecyl maleate, and bis(2,2-dimethylheptyl) maleate.
8. The process according to claim 1 , wherein the aluminum alkoxide has a general formula (II):
wherein R, R′, and R″ are the same or different hydrocarbyl radicals of not more than 12 carbon atoms.
9. The process according to claim 8 , wherein the aluminum alkoxide compound is selected from the group consisting of diethoxyaluminum butoxide, ethoxyaluminum dibutoxide, aluminum trimethoxide, aluminum triethoxide, aluminum tri-n-propoxide, aluminum triiso-propoxide, aluminum tri-n-butoxide, aluminum tri-sec-butoxide, and aluminum tri-t-butoxide.
10. The process according to claim 9 , wherein the aluminum alkoxide is aluminum triiso-propoxide.
11. The process according to claim 1 , wherein the siloxane mixture has a methyl group.
12. The process according to claim 11 , wherein the siloxane mixture is selected from the group consisting of octamethyltrisiloxane, decamethyltetrasiloxane, dodecamethylpentasiloxane, and polymethylsiloxane.