Multilayer sheet and methods of making and articles comprising the multilayer sheet
View Patent ↗In some embodiments, a multilayer sheet comprises: a first cap layer formed from a first cap composition comprising polycarbonate and potassium perfluorobutane sulfonate; a second cap layer formed from a second cap composition comprising polycarbonate and potassium perfluorobutane sulfonate; and a core layer formed from a core composition comprising polycarbonate and without potassium perfluorobutane sulfonate. The core layer is disposed between the first cap layer and the second cap layer.
1. A multilayer sheet, comprising:
a first cap layer formed from a first cap composition comprising potassium perfluorobutane sulfonate, 50wt % to 98wt % branched polycarbonate, and a brominated polycarbonate such that the first cap composition comprises 0.0125wt % to 2.5wt % bromine, based on the total weight of the first cap composition;
a second cap layer formed from a second cap composition comprising potassium perfluorobutane sulfonate, 50wt % to 98wt % branched polycarbonate, and a brominated polycarbonate such that the second cap composition comprises 0.0125wt % to 2.5wt % bromine, based on the total weight of the second cap composition; and
a core layer formed from a core composition comprising 50wt % to 98wt % branched polycarbonate and 0.5wt % to 5wt % brominated polycarbonate, based on the total weight of the core composition, and without potassium perfluorobutane sulfonate, wherein the core layer is disposed between the first cap layer and the second cap layer;
wherein the first cap composition comprises greater than or equal to 0.05wt % potassium perfluorobutane sulfonate, based upon a total weight of the first cap composition; and
wherein the second cap composition comprises greater than or equal to 0.05wt % potassium perfluorobutane sulfonate, based upon a total weight of the second cap composition;
wherein the multilayer sheet has a UL94 V 0 rating at a thickness of 1.8 mm; and wherein the multilayer sheet has a haze value of less than or equal to 1.5% as measured by ASTM D1003-00, Procedure A.
2. The multilayer sheet of claim 1 , wherein the amount of potassium perfluorobutane sulfonate in the multilayer sheet is less than 0.01 wt % based upon a total weight of the multilayer sheet.
3. The multilayer sheet of claim 1 , wherein the core composition comprises potassium diphenyl sulfone-3-sulfonate.
4. The multilayer sheet of claim 1 , wherein the first cap layer and/or the second cap layer have a thickness of less than or equal to 200 micrometers.
5. The multilayer sheet of claim 1 , wherein the core layer is co-extruded with the first cap layer and the second cap layer.
6. The multilayer sheet of claim 1 , wherein the first and/or second cap compositions further comprise an anti-dripping agent selected from the group consisting of PTFE, TSAN, and combinations comprising at least one of the foregoing.
7. The multilayer sheet of claim 1 , wherein the core layer has a thickness of less than or equal to 2 mm.
8. An article comprising the multilayer sheet of claim 1 .
9. The multilayer sheet of claim 1 , wherein the first cap composition and/or second cap composition comprises 60wt % to 80wt % branched polycarbonate, based on the total weight of the first cap composition and/or second cap composition, respectively.
10. The multilayer sheet of claim 9 , wherein the first cap composition and/or second cap composition comprises a brominated polycarbonate such that the first cap composition and/or second cap composition comprises 0.025wt % to 1.25wt % bromine, based on the total weight of the first cap composition and/or second cap composition, respectively.
11. The multilayer sheet of claim 1 , wherein the core composition comprises 60wt % to 80wt % branched polycarbonate, based on the total weight of the core composition.
12. The multilayer sheet of claim 11 , wherein the core composition comprises 1wt % to 2wt % brominated polycarbonate, based on the total weight of the core composition.
13. A method of making a multilayer sheet, comprising:
forming a core layer formed from a core composition comprising 50 wt % to 98wt % branched polycarbonate and 0.5wt % to 5wt% brominated polycarbonate, based on the total weight of the core composition and without potassium perfluorobutane sulfonate;
forming a first cap layer formed from a first cap composition comprising potassium perfluorobutane sulfonate, 50wt % to 98wt % branched polycarbonate, and a brominated polycarbonate such that the first cap composition comprises 0.0125wt% to 2.5wt% bromine, based on the total weight of the first cap composition, wherein the first cap layer is co-extruded onto a surface of the core layer; and
forming a second cap layer formed from a second cap composition comprising potassium perfluorobutane sulfonate, 50wt % to 98wt % branched polycarbonate, and a brominated polycarbonate such that the second cap composition comprises 0.0125wt % to 2.5wt % bromine, based on the total weight of the second cap composition wherein the second cap layer is co-extruded onto a surface of the core layer opposite the surface co-extruded with the first cap layer,
wherein the first cap composition comprises greater than or equal to 0.05wt % potassium perfluorobutane sulfonate, based upon a total weight of the first cap composition;
wherein the second cap composition comprises greater than or equal to 0.05wt % potassium perfluorobutane sulfonate, based upon a total weight of the second cap composition; and
wherein the multilayer sheet has a UL94 V 0 rating at a thickness of 1.8 mm; and wherein the multilayer sheet has a haze value of less than or equal to 1.5% as measured by ASTM D1003-00, Procedure A.