View Patent ↗Alkaline electrochemical cells having extended service life and acceptable gassing and corrosion properties are disclosed. An amphoteric surfactant can be incorporated into the gelled anode mixture of an alkaline electrochemical cell, optionally with an organic phosphate ester surfactant or a sulfonic acid type organic surfactant or both. Zinc particles having a defined distribution of particle sizes can also be incorporated into a zinc anode. The electrolyte included, in the anode mixture can have a reduced hydroxide concentration.
1. A gelled anode mixture comprising:
a metal alloy powder comprising zinc alloy particles, wherein between about 4 weight % and about 8 weight % of the zinc alloy particles have a particle size of less than about 75 micrometers,
a gelling agent,
an alkaline electrolyte having a hydroxide concentration between about 25 weight % and about 33 weight %, and
a phosphate ester surfactant present at a concentration ranging substantially between about 0.0004 weight % and about 0.0075 weight % relative to the gelled anode mixture.
2. A gelled anode mixture as claimed in claim 1 , wherein about 8 weight % of the zinc alloy particles have a particle size of less than about 75 micrometers.
3. A gelled anode mixture as claimed in claim 1 , wherein between about 4 weight % and about 8 weight % of the zinc alloy particles have a particle size between about 20 micrometers and about 75 micrometers.
4. A gelled anode mixture as claimed in claim 1 , wherein the hydroxide concentration is between about 25 weight % and about 30 weight %.
5. A gelled anode mixture as claimed in claim 1 , wherein the electrolyte comprises KOH.
6. A gelled anode mixture as claimed in claim 1 , wherein the surfactant is present at a concentration of about 0.0024 weight % relative to the gelled anode mixture.
7. A gelled anode mixture as claimed in claim 1 , wherein about 8 weight % of the zinc alloy particles have a particle size of less than about 75 micrometers, wherein the hydroxide concentration is between about 25 weight % and about 30 weight %, wherein the electrolyte comprises KOH, and wherein the surfactant is present at a concentration of about 0.0024 weight % relative to the gelled anode mixture.
8. An alkaline electrochemical cell comprising:
a positive current collector;
a cathode in contact with the positive current collector;
a gelled anode mixture comprising a metal alloy powder comprising zinc alloy particles, wherein between about 4 weight % and about 8 weight % of the zinc alloy particles have a particle size of less than about 75 micrometers, a gelling agent, an alkaline electrolyte having a hydroxide concentration between about 25 weight % and about 33 weight %, and a phosphate ester surfactant present at a concentration ranging substantially between about 0.0004 weight % and about 0.0075 weight % relative to the gelled anode mixture,
a separator between the cathode and the anode; and,
a negative current collector in electrical contact with the anode.
9. An alkaline electrochemical cell as claimed in claim 8 , wherein about 8 weight % of the zinc alloy particles have a particle size of less than about 75 micrometers.
10. An alkaline electrochemical cell as claimed in claim 8 , wherein between about 4 weight % and about 8 weight % of the zinc alloy particles have a particle size between about 20 micrometers and about 75 micrometers.
11. An alkaline electrochemical cell as claimed in claim 8 , wherein the hydroxide concentration is between about 25 weight % and about 30 weight %.
12. An alkaline electrochemical cell as claimed in claim 8 , wherein the electrolyte comprises KOH.
13. An alkaline electrochemical cell as claimed in claim 8 , wherein the surfactant is present at a concentration of about 0.0024 weight % relative to the gelled anode mixture.
14. An alkaline electrochemical cell as claimed in claim 8 , wherein about 8 weight % of the zinc alloy particles have a particle size of less than about 75 micrometers, wherein the hydroxide concentration is between about 25 weight % and about 30 weight %, wherein the electrolyte comprises KOH, and wherein the surfactant is present at a concentration of about 0.0024 weight % relative to the gelled anode mixture.