Process or manufacturing components obtained by sintering of Co-Cr-Mo alloys having improved ductility at high temperatures
View Patent ↗A process for manufacturing a component with a base of Co—Cr—Mo alloys having values of average ultimate elongation at 800° C. greater than 10% and of average yielding load at 800° C. greater than 400 MPa, comprising: obtaining a sintered component by additive sintering of powders of Co—Cr—Mo alloys containing carbides irregularly dispersed in the molten matrix; Conducting a first heat treatment on the sintered component for solubilization of the carbides at a temperature of between 1100° C. and 1300° C. for at least 2 hours to form a solubilization intermediate; and cooling the solubilization intermediate at a cooling rate at least equal to that of cooling in air to form a cooled intermediate; and conducting a second heat treatment on the cooled intermediate at a temperature of between 700° C. and 1000° C.
1. A process for manufacturing a high temperature component made from an alloy consisting essentially of 60-65% Co, 26-30% Cr and 5-7% Mo, comprising the steps of:
a) additively sintering powders of the alloy to obtain a sintered component containing Cr and Mo carbides dispersed in a Co-based molten matrix;
b) forming a solubilized intermediate by heat treating the sintered component at a temperature of between 1100 and 1300° C. for a treatment time of at least 2 hours;
c) cooling the solubilized intermediate in still air to form a cooled intermediate; and
d) heat treating the cooled intermediate at a temperature of between 700 and 1000° C.
2. The process according to claim 1 , wherein the treatment time in said step b) is at least 4 hours.
3. The process according to claim 1 , wherein the treatment temperature in said step b) is between 1200 and 1250 ° C.
4. The process according to claim 1 , wherein said step c) of cooling comprises a first step of cooling in the furnace such as to allow the temperature to decrease below 1100° C. and a second step of cooling in a flow of cooling gas.
5. The process according to claim 1 , wherein the treatment temperature in said step d) is between 800° C. and 830° C.
6. The process according to claim 1 , wherein the treatment time in said step d) is between 5 and 15 hours.
7. The process according to claim 1 , characterized in that said component is a part of a gas turbine combustor.
8. The process as in claim 1 wherein the cooling undertaken in step c) cools to a point that prevents re-precipitation of the Cr and Mo carbides.
9. The process as in claim 1 , wherein the high temperature component has an average ultimate elongation at 800° C. greater than 10% and an average yielding load at 800° C. greater than 400 MPa.