Heterophasic polypropylene with high flowability and excellent low temperature impact properties

1. Heterophasic polypropylene resin comprising

a propylene homo- or copolymer matrix (A) and an ethylene propylene rubber phase (B) dispersed within the matrix,

wherein the heterophasic polypropylene resin has

a fraction insoluble in p-xylene at 25° C. (XCU) with an intrinsic viscosity of 1.5 dl/g or less, determined according to DIN EN ISO 1628-1 and -3 and an amount of propylene monomer units of at least 95 mol %, and

a fraction soluble in p-xylene at 25° C. (XCS) with an intrinsic viscosity of 1.5 to 3.0 dl/g, determined according to DIN EN ISO 1628-1 and -3, and an amount of propylene monomer units of 50 to 75 mol %, and a molecular weight distribution MWD of 2.5 to 3.5,

and a MFR (2.16 kg, 230° C.) of more than 100 g/10 min, determined according to ISO 1133,

wherein the XCU fraction is present in an amount of 70 to 90 wt % of the heterophasic polypropylene resin and the XCS fraction is present in an amount of 10 to 30 wt % of the heterophasic polypropylene resin.

2. Heterophasic polypropylene resin according to claim 1 wherein the XCU fraction has a weight average molecular weight Mw of 50 to 200 kg/mol, measured by GPC according to ISO 16014-1, and 4.

3. Heterophasic polypropylene resin according to claim 1 wherein the XCU fraction has a molecular weight distribution MWD of 1.5 to 5.0.

4. Heterophasic polypropylene resin according to claim 1 wherein the XCS fraction has a weight average molecular weight Mw of 80 to 300 kg/mol measured by GPC according to ISO 16014-1, and 4.

5. Heterophasic polypropylene resin according to claim 1 wherein the resin has a Charpy notched impact strength at +23° C. of at least 5.0 kJ/m 2 , determined according to ISO 179-1/1 eA.

6. Heterophasic polypropylene resin according to claim 1 wherein the resin has a Charpy notched impact strength at 0° C. of at least 4.0 kJ/m 2 , determined according to ISO 179-1/1 eA.

7. Heterophasic polypropylene resin according to claim 1 wherein the resin has a Charpy notched impact strength at −20° C. of at least 3.0 kJ/m 2 , determined according to ISO 179-1/1 eA.

8. Heterophasic polypropylene resin according to claim 1 wherein the resin has an instrumented falling weight impact at +23° C. of at least 11 J, determined according to ISO 6603-2.

9. Heterophasic polypropylene resin according to claim 1 wherein the resin has been produced in a multistage process.

10. Heterophasic polypropylene resin according to claim 1 wherein the resin has been produced in presence of a catalyst System comprising an asymmetric catalyst wherein the catalyst System has a porosity of less than 1.40 ml/g.

11. Heterophasic polypropylene resin according to claim 10 wherein the asymmetric catalyst is dimethylsilyl [(2-methyl-(4′-tert.butyl)-4-phenyl-indenyl) (2-isopropyl-(4′-tert.butyl)-4-phenyl-indenyl)]-zirconium dichloride.

12. Process for the production of a heterophasic polypropylene resin according to claim 1 wherein the propylene homo- or copolymer matrix phase (A) is prepared in a first stage, and the ethylene-propylene rubber phase (B) is prepared in a second stage in presence of the first stage product.

13. Heterophasic polypropylene composition comprising a heterophasic polypropylene resin according to claim 1 and modifiers in an amount of up to 10 wt % as well as additives of up to 1 wt %.

14. Article comprising the heterophasic polypropylene resin according to claim 1 or the heterophasic polypropylene composition according to claim 13 .

15. Article comprising the heterophasic polypropylene composition according to claim 13 .