WATER-BORNE EPOXY RESIN SYSTEMS
This invention is directed to two-pack coating compositions comprising epoxy resins B having at least one epoxide group per molecule, and adducts A of epoxy resins A1 having at least one epoxide group per molecule and of multifunctional A2 acids having at least two acidic hydrogen groups per molecule, a process for their preparation, and a method of use thereof in coating of substrates.
1 . Two-pack coating compositions comprising epoxy resins B having at least one epoxide group per molecule, and adducts A of epoxy resins A1 having at least one epoxide group per molecule and of multifunctional A2 acids having at least two acidic hydrogen groups per molecule, wherein the multifunctional acids A2 are addition products of epoxy functional compounds A21 having at least one epoxide group per molecule, and acids A22 selected from the group consisting of inorganic acids derived from phosphorus or from sulphur, and of organic acids derived from phosphorus or from sulphur.
2 . The two-pack coating compositions of claim 1 wherein the multifunctional acids A2 have phosphorus-based acid groups.
3 . The two-pack coating compositions of claim 1 wherein the acids A22 selected from the group consisting of inorganic acids derived from phosphorus, and of organic acids derived from phosphorus.
4 . The two-pack coating compositions of claim 1 wherein the multifunctional acids A2 are addition products of phosphoric acid and epoxy functional compounds A21 having at least one epoxide group per molecule.
5 . The two-pack coating compositions of claim 1 wherein the adducts A have a Staudinger index, measured in accordance with DIN 1342, part 2.4, in dimethylformamide as solvent, of from 8 cm 3 /g to 20 cm 3 /g.
6 . The two-pack coating compositions of claim 1 wherein the mass ratio of the epoxy resins B to the adducts A is from 9:1 to 1:1.
7 . A process to prepare the two-pack coating compositions of claim 1 , comprising the steps of
charging a solution of an epoxy resin A1 in an organic water-miscible solvent,
adding thereto an addition product A2 of an epoxy functional compound A21 having at least one epoxide group per molecule, and an acid A22
reacting the mixture until the epoxide groups are consumed, to form an adduct A,
mixing the adduct A to an epoxy resin B.
8 . The process of claim 7 wherein the adduct A is neutralised with a tertiary amine and then dispersed in water, and then mixed with an aqueous dispersion of an epoxy resin B.
9 . A method of use of the two-pack coating composition of claim 1 , comprising applying the coating composition to a substrate selected from the group consisting of green concrete, plaster, stone, wood, particle boards, and base metals.
10 . The method of claim 9 where the coating composition is applied to green concrete before the onset of hydraulic hardening.