Process for preparing silver-containing aqueous formulation useful for electrically conductive or reflective coatings
View Patent ↗Process for preparing A silver-containing, disperse, water-containing formulation useful for producing electrically conductive and/or optically reflective coatings, which comprises (i) reacting a silver salt solution with a solution containing hydroxide ions, wherein at least one of said solutions comprises a polymeric dispersant, to produce an Ag 2 O sol, (ii) reacting the Ag 2 O sol obtained from step i) with a reduction agent, and (iii) purifying the solution obtained from step ii).
1. A process for preparing a silver-containing, disperse, water-containing formulation containing at least
a) 0.5 to 30 parts by wt. of silver metal particles with an effective diameter of at most 150 nm with a bimodal size distribution of the silver metal particles, determined using laser correlation spectroscopy,
b) 50 to 99.5 parts by wt. of water and optionally up to 30 parts by wt. of solvent,
c) 0.01 to 10 parts by wt. of at least one polymeric, dispersant,
d) 0 to 5 parts by wt. of film-producer,
e) 0 to 5 parts by wt. of additives,
f) 0 to 5 parts by wt. of conductive polymers, said formulation having a viscosity of at most 150 mPa·s,
comprising the steps of
i) reacting a silver salt solution with a solution containing hydroxide ions, wherein at least one of said solutions comprises a polymeric dispersant, to produce an Ag 2 O sol,
ii) reacting the Ag 2 O sol obtained from step i) with a reduction agent,
iii) purifying the solution obtained from step ii) by centrifugation or membrane filtration.
2. The process of claim 1 , wherein said silver salt is silver nitrate and said hydroxide is sodium hydroxide.
3. The process of claim 1 , where said reducing agent is an aqueous formaldehyde solution.
4. The process of claim 1 , wherein said purification is by membrane filtration.
5. The process of claim 1 , wherein said dispersant is at least one agent selected from the group consisting of polyvinyl alcohols, copolymers of polyvinyl alcohols and polyvinyl acetates, polyvinylpyrrolidones, cellulose, starch, gelatine, gelatine derivatives, polymers of amino acids, polylysine, polyaspartic acid, polyacrylates, polyethylene sulfonates, polystyrene sulfonates, polymethacrylates, condensation products of aromatic sulfonic acids and formaldehyde, naphthalene sulfonates, lignin sulfonates, copolymers of acrylic monomers, polyethylenimines, polyvinylamines, polyallylamines, poly(2-vinylpyridines), block copolyethers, block copolyethers with polystyrene blocks, polydiallyldimethylammonium chloride and combinations thereof.
6. The process of claim 1 , wherein after step ii) but before step iii), particles are separated from the solution.
7. The process of claim 6 wherein said particles are separated from said solution by diafiltration.