Multi-Layer Sheet Structure Including An Acrylic Outer Layer
A multi-layer sheet structure, in an exemplary embodiment, includes a first layer of a thermoplastic olefin (TPO) composition that includes polypropylene and a filler, and a second layer that includes a polyolefin composition. The second layer positioned over at least a portion of the first layer. The multi-layer sheet structure also includes a third layer that includes an adhesive, and a fourth layer that includes a transparent acrylic composition. The third layer is between the second layer and the fourth layer.
1 . A multi-layer sheet structure comprising:
a first layer comprising a thermoplastic olefin (TPO) composition comprising polypropylene and a filler;
a second layer comprising a polyolefin composition, said second layer over at least a portion of said first layer;
a third layer comprising an adhesive; and
a fourth layer comprising a transparent acrylic composition, said third layer between said second layer and said fourth layer.
2 . A multi-layer sheet structure in accordance with claim 1 wherein said polypropylene comprises at least one of a propylene homopolymer, a random polypropylene co-polymer formed with alpha-olefins, and an impact polypropylene co-polymer with a discrete rubber phase based on ethylene or propylene co-polymer elastomers.
3 . A multi-layer sheet structure in accordance with claim 1 wherein said filler comprises at least one of talc, calcium carbonate, mica, fibrous materials, glass fibers, natural fibers, mineral fillers, wollastonite, silicate, carbon black and clays.
4 . A multi-layer sheet structure in accordance with claim 1 wherein said TPO composition further comprises an elastomer.
5 . A multi-layer sheet structure in accordance with claim 4 wherein said elastomer comprises polyethylene co-polymers with propylene, butene, hexene, octene, ethylidene norbornene and alpha-olefin co-monomers.
6 . A multi-layer sheet structure in accordance with claim 1 wherein said TPO composition further comprises at least one of anti-oxidants, process aids, pigments, dyes, light stabilizers, heat stabilizers, and lubricants.
7 . A multi-layer sheet structure in accordance with claim 1 wherein said polyolefin composition of said second layer comprises at least one of a propylene homopolymer, a random polypropylene co-polymer formed with alpha-olefins, and an impact polypropylene co-polymer with a discrete rubber phase based on ethylene or propylene co-polymer elastomers.
8 . A multi-layer sheet structure in accordance with claim 1 wherein said transparent acrylic composition comprises an alkyl (meth)acrylate polymer composition.
9 . A multi-layer sheet structure in accordance with claim 8 wherein said alkyl (meth)acrylate polymer composition comprises at least one of methyl acrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, propyl acrylate, propyl methacrylate, n-butyl acrylate, n-butyl methacrylate, and copolymers thereof.
10 . A multi-layer sheet structure in accordance with claim 1 wherein said adhesive comprises a heat activated adhesive.
11 . A method of making a multi-layer sheet structure, said method comprising:
co-extruding a TPO composition and a polypropylene composition to form a layered structure comprising a TPO layer and a polypropylene layer, the TPO composition comprising a polypropylene and a filler;
providing a transparent acrylic film;
applying an adhesive onto at least one of a surface of the polypropylene layer and a surface of the transparent acrylic film; and
applying the transparent acrylic film to the polypropylene layer with the adhesive between the acrylic film and the polypropylene layer.
12 . A method of making a multi-layer sheet structure in accordance with claim 11 wherein the polypropylene comprises at least one of a propylene homopolymer, a random polypropylene co-polymer formed with alpha-olefins, and an impact polypropylene co-polymer with a discrete rubber phase based on ethylene or propylene co-polymer elastomers.
13 . A method of making a multi-layer sheet structure in accordance with claim 11 wherein the filler comprises at least one of talc, calcium carbonate, mica, fibrous materials, glass fibers, natural fibers, mineral fillers, wollastonite, silicate, carbon black and clays.
14 . A method of making a multi-layer sheet structure in accordance with claim 11 wherein the TPO composition further comprises an elastomer.
15 . A method of making a multi-layer sheet structure in accordance with claim 14 wherein the elastomer comprises polyethylene co-polymers with propylene, butene, hexene, octene, ethylidene norbornene and alpha-olefin co-monomers.
16 . A method of making a multi-layer sheet structure in accordance with claim 11 wherein said TPO composition further comprises at least one of anti-oxidants, process aids, pigments, dyes, light stabilizers, heat stabilizers, and lubricants.
17 . A method of making a multi-layer sheet structure in accordance with claim 11 wherein the polyolefin composition comprises at least one of a propylene homopolymer, a random polypropylene co-polymer formed with alpha-olefins, and an impact polypropylene co-polymer with a discrete rubber phase based on ethylene or propylene co-polymer elastomers.
18 . A method of making a multi-layer sheet structure in accordance with claim 11 wherein applying an adhesive comprises applying an adhesive by at least one of spraying the adhesive onto at least one of a surface of the polypropylene layer and a surface of the transparent acrylic film, and roll coating the adhesive onto at least one of a surface of the polypropylene layer and a surface of the transparent acrylic film.
19 . A method of making a multi-layer sheet structure in accordance with claim 11 wherein applying an adhesive comprises applying an adhesive by at least one of spraying the adhesive onto a surface of the transparent acrylic film, and roll coating the adhesive onto a surface of the transparent acrylic film; and
applying the transparent acrylic film to the polypropylene layer comprises laminating the adhesive coated transparent acrylic film to the polypropylene layer with the adhesive between the transparent acrylic film and the polypropylene layer.
20 . A method of making a multi-layer sheet structure in accordance with claim 11 wherein the adhesive is an extruded sheet, and applying an adhesive comprises positioning the extruded sheet of adhesive between the polypropylene layer and the transparent acrylic film.
21 . A multi-layer TPO sheet structure comprising:
a propylene based TPO substrate layer comprising polypropylene and a filler;
a polypropylene cap layer bonded to said TPO substrate layer;
a transparent acrylic layer; and
an adhesive between said polypropylene cap layer and said transparent acrylic layer to bond said transparent acrylic layer to said polypropylene cap layer.
22 . A multi-layer TPO sheet structure in accordance with claim 21 wherein said polypropylene comprises at least one of a propylene homopolymer, a random polypropylene co-polymer formed with alpha-olefins, and an impact polypropylene co-polymer with a discrete rubber phase based on ethylene or propylene co-polymer elastomers.
23 . A multi-layer TPO sheet structure in accordance with claim 21 wherein said filler comprises at least one of talc, calcium carbonate, mica, fibrous materials, glass fibers, natural fibers, mineral fillers, wollastonite, silicate, carbon black and clays.
24 . A multi-layer TPO sheet structure in accordance with claim 21 wherein said TPO substrate layer further comprises an elastomer.
25 . A multi-layer sheet structure in accordance with claim 24 wherein said elastomer comprises polyethylene co-polymers with propylene, butene, hexene, octene, ethylidene norbornene and alpha-olefin co-monomers.
26 . A multi-layer sheet structure in accordance with claim 21 wherein said TPO composition further comprises at least one of anti-oxidants, process aids, pigments, dyes, light stabilizers, heat stabilizers, and lubricants.
27 . A multi-layer TPO sheet structure in accordance with claim 21 wherein said polypropylene cap layer comprises at least one of a propylene homopolymer, a random polypropylene co-polymer formed with alpha-olefins, and an impact polypropylene co-polymer with a discrete rubber phase based on ethylene or propylene co-polymer elastomers.
28 . A multi-layer TPO sheet structure in accordance with claim 21 wherein said transparent acrylic composition comprises an alkyl (meth)acrylate polymer composition.
29 . A multi-layer TPO sheet structure in accordance with claim 28 wherein said alkyl (meth)acrylate polymer composition comprises at least one of methyl acrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, propyl acrylate, propyl methacrylate, n-butyl acrylate, n-butyl methacrylate, and copolymers thereof.
30 . A multi-layer TPO sheet structure in accordance with claim 21 wherein said adhesive comprises a heat activated adhesive.
31 . A method of making a multi-layer TPO sheet structure, said method comprising:
extruding a sheet of a TPO layer comprising polypropylene and a filler;
extruding a polypropylene layer onto the TPO layer;
providing a transparent acrylic film;
applying an adhesive on at least one of the polypropylene layer and the transparent acrylic film; and
applying the transparent acrylic film onto the polypropylene layer.
32 . A method of making a multi-layer TPO sheet structure in accordance with claim 31 wherein the polypropylene comprises at least one of a propylene homopolymer, a random polypropylene co-polymer formed with alpha-olefins, and an impact polypropylene co-polymer with a discrete rubber phase based on ethylene or propylene co-polymer elastomers.
33 . A method of making a multi-layer TPO sheet structure in accordance with claim 31 wherein applying an adhesive comprises applying an adhesive by at least one of spraying the adhesive onto a surface of the transparent acrylic film, and roll coating the adhesive onto a surface of the transparent acrylic film; and
applying the transparent acrylic film to the polypropylene layer comprises laminating the adhesive coated transparent acrylic film to the polypropylene layer with the adhesive between the transparent acrylic film and the polypropylene layer.
34 . A method of making a multi-layer TPO sheet structure, said method comprising:
extruding a sheet of a TPO layer comprising polypropylene and a filler;
extruding a polypropylene layer onto the TPO layer;
extruding an adhesive layer onto the polypropylene layer; and
extruding a transparent acrylic film onto the adhesive layer.
35 . A method of making a multi-layer TPO sheet structure in accordance with claim 34 wherein the polypropylene comprises at least one of a propylene homopolymer, a random polypropylene co-polymer formed with alpha-olefins, and an impact polypropylene co-polymer with a discrete rubber phase based on ethylene or propylene co-polymer elastomers.