Compositions and methods for treating bone
View Patent ↗The present invention relates to compositions, methods and kits for the treatment of bone particularly impaired or damaged bone.
1. A method of treating bone comprising applying a composition to the bone, wherein
the composition comprises a solution comprising platelet-derived growth factor (PDGF) at a concentration in a range of 0.1 to 1.0 mg/mL in a buffer disposed in a biocompatible matrix;
the biocompatible matrix is selected from the group consisting of i) particles of β-tricalcium phosphate having interconnected pores, and ii) particles β-tricalcium phosphate having interconnected pores and collagen;
the β-tricalcium phosphate comprises pores and has a porosity greater than 50%;
the particles of β-tricalcium phosphate have an average diameter ranging from 1 μm to 5 mm and,
the bone is a fractured bone, an osteoporotic bone, a weakened bone, or a bone susceptible to damage due to increased compensatory load.
2. The method of claim 1 , further comprising: applying the composition to orthopedic hardware; and, inserting the orthopedic hardware into the bone.
3. The method of claim 1 , wherein the PDGF is PDGF-AA, PDGF-BB, PDGF-AB, PDGF-CC, or PDGF-DD, or a mixture thereof.
4. The method of claim 1 , wherein the PDGF is rhPDGF-BB or a fragment thereof.
5. The method of claim 1 , wherein the solution has a pH ranging from 3.0 to 8.0.
6. The method of claim 1 , wherein the β-tricalcium phosphate has a calcium/phosphorous atomic ratio ranging from 0.5 to 2.0.
7. The method of claim 1 , wherein the β-tricalcium phosphate comprises pores having diameters ranging from 1 μm to 1 mm.
8. The method of claim 1 , wherein the β-tricalcium phosphate comprises particles having an average diameter ranging from 200 μm to 3000 μm.
9. The method of claim 1 , wherein the particles of β-tricalcium phosphate have an average diameter in a range of 250 μm to 750 μm.
10. The method of claim 1 , wherein the biocompatible matrix is the particles of β-tricalcium phosphate.
11. The method of claim 1 , wherein the biocompatible is the particles of β-tricalcium phosphate and collagen.
12. The method of claim 11 , wherein the collagen is present in an amount ranging from 15 weight percent to 35 weight percent of the biocompatible matrix.
13. The method of claim 12 , wherein the composition is flowable.
14. The method of claim 1 , wherein the biocompatible matrix comprises particles of β-tricalcium phosphate having a diameter ranging from 75 μm to 300 μm, and the biocompatible matrix further comprises 15 to 35% by weight of collagen.
15. The method of claim 14 , wherein the PDGF has a concentration in a range of 0.25 to 0.5 mg/mL.
16. The method of claim 1 , wherein the composition further comprises a contrast agent, one or more biologically active agents, or a mixture thereof.
17. The method of claim 1 , wherein the bone is a humerus, ulna, radius, femur, tibia, fibula, patella, ankle bone, wrist bone, carpal, metacarpal, phalangeal, tarsal, metatarsal, rib, sternum, vertebra, scapula, clavicle, pelvis, or sacrum.