Composite article made by a process
View Patent ↗Disclosed herein is a consolidated or densified composite article comprising polymer, particularly fluoropolymer, and carbon fiber.
1. A consolidated composite article having a density, Dc, and comprising: (i) a polymer having a softening temperature and (ii) fibers, said composite article produced by:
providing a matte, wherein said matte is a mixture comprising: from about 1 wt % to about 90 weight percent of said fibers; and from about 10 weight percent to about 90 weight percent particles of a polymer, said matte having a density, Dm, that is less than Dc;
densifying said matte to a compressed density greater than 1.1 times Dm and less than 0.999 times Dc while at least a portion of said matte is at a temperature less than softening temperature of polymer, to provide a compressed matte;
heating said compressed matte throughout to a temperature greater than said softening temperature at a density greater than 1.1 times Dm and less than 0.999 times Dc, to provide a preconsolidated matte;
cooling at least a portion of said preconsolidated matte to a temperature less than said softening temperature, to provide a consolidated matte;
stacking a plurality of said consolidated matte to provide an article having fiber orientation of each immediately adjacent and contacting matte at right angles;
compressing the height of said article and heating throughout to a temperature greater than said softening temperature, to provide a consolidated composite article; and
cooling at least a portion of said consolidated composite article to a temperature less than said softening temperature.
2. The composite article of claim 1 wherein said polymer is selected from fluoropolymer or polymers comprising repeat units or monomers of tetrafluoroethylene, perfluoro (alkoxyalkane) of 3 to 14 carbon atoms.
3. The composite article of claim 2 wherein said polymer is selected from the group consisting of perfluoro(vinyl propyl ether), hexafluoropropylene, chlorotrifluoroethylene, ethylene, propylene, and combinations thereof.
4. The composite article of claim 1 wherein said polymer comprises (tetrafluoroethylene-perfluoro(propyl vinyl ether) copolymer.
5. The composite article of claim 1 wherein said fibers are selected from the group consisting of glass, graphite, carbon; fluorinated graphite; aramid, boron nitride; silicon carbide; polyester; and polyamide.
6. The composite article of claim 1 or 4 wherein said fibers are chopped fibers.