Polytrimethylene ether glycol esters
View Patent ↗Disclosed are processes to prepare monocarboxylic acid esters (mono- and/or diesters) of polytrimethylene ether glycol that are substantially free of residues from the catalyst used to produce the polytrimethylene ether glycol esters, as well as methods for their preparation and end uses thereof. The esters, such as the bis-2-ethylhexanoate esters, have uses as functional fluids.
1. A process for preparing a composition comprising a polytrimethylene ether glycol ester comprising:
(a) polycondensing, a hydroxyl groups containing reactant comprising at least 50 mole % 1,3-propanediol in the presence sulfuric acid to obtain a polytrimethylene ether glycol composition;
(b) esterifying, the polytrimethylene ether glycol composition by heating it with a monocarboxylic acid of the formula R—COOH, wherein R is an organic group containing from 6 to 40 carbon atoms, and/or a monocarboxylic acid equivalent thereof, in the presence of sulfuric acid to obtain a crude polytrimethylene ether glycol ester containing a residual sulfuric acid ester;
(c) hydrolyzing the residual sulfuric acid ester of the crude ester by heating with water at a temperature from 80° C. to 100° C. for 1 to 8 hours, wherein water is present in the 20 weight percent relative to the total weight of the water and crude ester; and
(d) removing the water to obtain a polytrimethylene ether glycol ester that has less than 20 ppm of residual sulfur, and wherein the process steps (a), (b), (c) and (d) are carried out in the absence of an organic solvent.
2. The process of claim 1 , wherein the monocarboxylic acid comprises 2-ethylhexanoic acid, benzoic acid, stearic acid and/or oleic acid.
3. The process of claim 1 , wherein the polytrimethylene ether glycol ester comprises from about 50 to 100 wt % diester and from 0 to about 50 wt % monoester, based on the weight of the polytrimethylene ether glycol ester.
4. The process of claim 1 , wherein the 1,3-propanediol is produced by a fermentation process using a renewable biological source.
5. The process of claim 1 , wherein the number average molecular weight of the polytrimethylene ether glycol is from about 250 to about 5000.