Modified catalyst supports
View Patent ↗A modified catalyst support exhibiting attrition resistance and/or deaggregation resistance is provided. A catalyst composition including the modified catalyst support is also provided. A process to produce a modified catalyst support including treatment of a support slurry with a solution of monosilicic acid is provided. A process to use a catalyst including the modified catalyst support in a Fischer-Tropsch synthesis is provided.
1. A method of preparing an improved Fischer-Tropsch catalyst, comprising the steps of:
contacting an alumina support material with monosilicic acid to provide a treated catalyst support having between about 0.3 atoms Si/nm 2 and about 6.2 atoms Si/nm 2 deposited thereon wherein the Si atoms are bound directly to the alumina through an oxygen atom; and
impregnating the treated catalyst support with a material selected from the group consisting of cobalt, ruthenium, lanthanum, and combinations thereof to form the Fischer-Tropsch catalyst.
2. The method of claim 1 wherein the monosilicic acid contacts the alumina support material at a temperature between about 0° C. and about 95° C.
3. The method of claim 1 wherein the monosilicic acid contacts the alumina support material such that the pH is between about 1.5 and about 3.5.
4. The method of claim 1 wherein the silicon is deposited on the alumina support material between about 0.55 atoms Si/nm 2 and about 5.0 atoms Si/nm 2 .
5. The method of claim 1 wherein the silicon is deposited on the alumina support material between about 0.70 atoms Si/nm 2 and about 3.5 atoms Si/nm 2 .
6. The method of claim 1 wherein the alumina support material is preformed.
7. The method of claim 1 further comprising the step of:
drying the treated catalyst support at a temperature between about 100° C. and about 200° C.
8. The method of claim 1 wherein the amount of cobalt is between about 10.0% by weight and about 30.0% by weight based on the total weight of the Fischer-Tropsch catalyst.
9. The method of claim 1 wherein the amount of ruthenium is between about 0.03% by weight and about 0.30% by weight based on the total weight of the Fischer-Tropsch catalyst.
10. The method of claim 1 wherein the amount of lanthanum is between about 0.5% by weight and about 2.0% by weight based on the total weight of the Fischer-Tropsch catalyst.
11. The method of claim 1 further comprising the step of:
calcining the Fischer-Tropsch catalyst at a temperature of between about 250° C. and about 500° C.
12. The method of claim 1 wherein the Fischer-Tropsch catalyst is regenerated.
13. The method of claim 1 wherein the Fischer-Tropsch catalyst is greater than 99% free of particles having a diameter less than 20 μm.
14. A method of preparing an improved Fischer-Tropsch catalyst, comprising the steps of:
contacting an alumina support material with monosilicic acid thereby to provide a treated catalyst support having between about 0.3 atoms Si/nm 2 and about 10.6 atoms Si/nm 2 deposited thereon wherein the Si atoms are bound directly to the alumina through an oxygen atom; and
impregnating the treated catalyst support with a material selected from the group consisting of a Group VIII metal, a modifier, an activator, and combinations thereof to form the Fischer-Tropsch catalyst.
15. The method of claim 14 wherein the Group VIII metal is present between about 10.0% by weight and about 30.0% by weight based on the material which impregnates the treated catalyst support.
16. The method of claim 15 wherein the Group VIII metal is cobalt.
17. The method of claim 14 wherein the modifier is selected from the group consisting of Ca, Sc, Ba, La, Hf, and combinations thereof.
18. The method of claim 14 wherein the activator is selected from the group consisting of Ru, Rh, Pd, Re, Ir, Pt, and combinations thereof.
19. The method of claim 14 wherein the Fischer-Tropsch catalyst is greater than 99% free of particles having a diameter less than 20 μm.
20. A method of preparing an improved Fischer-Tropsch catalyst, comprising the steps of:
contacting an alumina support material with monosilicic acid at a pH between about 2.2 to about 2.5 thereby to provide a treated catalyst support having between about 0.3 atoms Si/nm 2 and about 6.2 atoms Si/nm 2 deposited thereon wherein the Si atoms are bound directly to the alumina through an oxygen atom;
drying the treated catalyst support at a temperature between about 100° C. and about 150° C.; and
impregnating the treated catalyst support with at least about 20% by weight of cobalt, at least about 0.1% by weight of ruthenium, at least about 1.0% by weight of lanthanum, and combinations thereof based on the total weight of the Fischer-Tropsch catalyst.