The present invention is to provide a TiO 2 —SiO 2 glass having suitable thermal expansion properties as an optical member of an exposure tool for EUVL. The present invention relates to a TiO 2 -containing silica glass having a temperature, at which a coefficient of thermal expansion is 0 ppb/° C., falling within the range of 23±4° C. and a temperature width, in which a coefficient of thermal expansion is 0±5 ppb/° C., of 5° C. or more.
1. A TiO 2 -containing silica glass having a temperature, at which a coefficient of thermal expansion is 0 ppb/° C., falling within a range of 23±4° C., a temperature width, in which a coefficient of thermal expansion is 0±5 ppb/° C., of 5° C. or more, and an OH concentration of 100 ppm or more.
2. The TiO 2 -containing silica glass according to claim 1 , having a fictive temperature of not higher than 850° C., and a TiO 2 content of from 3 to 9% by mass.
3. The TiO 2 -containing silica glass according to claim 1 , wherein the temperature, at which a coefficient of thermal expansion is 0 ppb/° C., is within a range of 22 ±2° C.
4. The TiO 2 -containing silica glass according to claim 1 , wherein the temperature width, in which a coefficient of thermal expansion is 0±5 ppb/° C., is 6° C. or more.
5. The TiO 2 -containing silica glass according to claim 1 , wherein the temperature width, in which a coefficient of thermal expansion is 0±5 ppb/° C., is 7.8° C. or more.
6. The TiO 2 -containing silica glass according to claim 1 , wherein the OH concentration is 200 ppm or more.
7. A TiO 2 -containing silica glass having a temperature, at which a coefficient of thermal expansion is 0 ppb/° C., falling within a range of 23±4° C., a temperature width, in which a coefficient of thermal expansion is 0±5 ppb/° C., of 5° C. or more, a fictive temperature of not higher than 850° C., and an F concentration of 1,000 ppm or more.
8. The TiO 2 -containing silica glass according to claim 7 , having a TiO 2 content of from 3 to 9% by mass.
9. The TiO 2 -containing silica glass according to claim 7 , wherein the temperature, at which a coefficient of thermal expansion is 0 ppb/° C., is within a range of 22 ±2° C.
10. The TiO 2 -containing silica glass according to claim 7 , wherein the temperature width, in which a coefficient of thermal expansion is 0±5 ppb/° C., is 6° C. or more.
11. The TiO 2 -containing silica glass according to claim 7 , wherein the temperature width, in which a coefficient of thermal expansion is 0±5 ppb/° C., is 8° C. or more.