Multilayer structure useful for electrical insulation
View Patent ↗A multilayer structure particularly useful in a transformer which contains (a) a first layer of aramid and cellulose wherein (i) the aramid is present as an meta-aramid in an amount of 0 to 50 weight percent floc and 50 to 100 weight percent fibrid, (ii) the cellulose is present in the form of cellulosic pulp fiber and (iii) the aramid is present in an amount of 16 to 75 weight percent and the cellulose is present in an amount of 25 to 84 weight percent, said percentages on the basis of the aramid and cellulose and (b) a second layer containing cellulosic pulp fiber with the proviso that the second layer does not contain aramid.
1. A transformer comprising an electrical conductor and an electrically insulating multilayer paper structure material comprising in order
(a) a first layer containing aramid and cellulose wherein
(i) the aramid is present as act a meta-aramid in an amount of 0 to 50 weight percent floc and 50 to 100 weight percent fibrid,
(ii) the cellulose is present in the form of cellulosic pulp fiber and
(iii) the aramid is present in an amount of 16 to 75 weight percent and
the cellulose is present in an amount of 25 to 84 weight percent
said percentages on the basis of the aramid and cellulose and
(b) a second layer containing cellulosic pulp fiber with the proviso that the second layer does not contain aramid,
(c) a third layer containing aramid and cellulose wherein
(i) the aramid is present as a meta-aramid in an amount of 0 to 50 weight percent floc and 50 to 100 weight percent fibrid,
(ii) the cellulose is present in the form of cellulosic pulp fiber and
(iii) the aramid is present in an amount of 16 to 75 weight percent and
the cellulose is present in an amount of 25 to 84 weight percent,
said percentages on the basis of the aramid and cellulose,
wherein the paper structure material is wrapped around an electrical conducting coil of the transformer and,
wherein the first layer containing aramid and cellulose contacts the electrically conducting coil and wherein the first layer does not contain polymeric binder.
2. The transformer of claim 1 which is oil filled.
3. The transformer of claim 1 which has a capacity of at least 200 kVA.
4. The transformer of claim 3 which has a capacity of at least 400 kVA.
5. The transformer of claim 1 wherein the first layer and the third layer have the same aramid/cellulose ratio.
6. The transformer of claim 1 wherein the first layer and the third layer have different aramid/cellulose ratios.