Process for over-molding onto crosslinked polymers

1. A process for injection overmolding a second polymer onto a crosslinked profile of a first polymer comprising the steps of:

heating at least a portion of said crosslinked profile, said first polymer crosslinked to at least 65% to a temperature which raises the temperature of a skin of said portion of said first crosslinked profile from a first temperature to a second higher temperature for a duration sufficient to heat said crosslinked portion to said second temperature, said second temperature being below the temperature at which said first polymer begins to degrade, said crosslinked profile having been crosslinked from a method selected from the group consisting of radiation and silane, said second temperature of said skin of said portion of said crosslinked profile reaching a temperature of at least approximately 112° F. and less than approximately 269° F.;

inserting at least a portion of said heated portion of said crosslinked profile while said heated crosslinked profile portion is still in a heated condition, at least partially into a mold, said mold containing a void for receiving a second polymer, the void co-acting with the crosslinked profile to define an overmolding profile;

injection molding said second polymer over at least a portion of the heated portion of said crosslinked profile into the void of the mold; and

crosslinking said second polymer, an affixation between said heated portion of said crosslinked profile and said second crosslinked polymer being able to pass a hot burst pressure test applicable to an intended end use for said combination of said overmolded polymer and crosslinked profile at 180° F. in which increasing test pressure within the first and second profiles causes a burst failure without any visible separation between said first and second profiles after said test.

2. The process of claim 1 which further comprises the step of

crosslinking said second polymer from an initial degree of crosslinking to a final degree of crosslinking, said step of crosslinking said second polymer using a crosslinking methodology selected from the group consisting of radiation and silane.

3. The process of claim 1 wherein the step of inserting further comprises

at least partially positioning said crosslinked profile onto a mandrel.

4. The process of claim 1 wherein

the first and second polymers are polyethylene.

5. The process of claim 4 wherein

a final degree of crosslinking of said second polymer is greater than 65%.

6. The process of claim 5 wherein

a final degree of crosslinking of said second polymer is greater than 70%.

7. The process of claim 1 wherein

said second polymer is at least partially crosslinked before the step of crosslinking.

8. The process of claim 4 wherein

said first and second polymers are crosslinked to approximately the same final degree.

9. A process for injection overmolding crosslinked tubes comprising the steps of:

heating at least a portion of a skin surface of a tube of a first polymer crosslinked to at least 65% with a heating means to at least approximately 112° F. and less than approximately 269° F. so that said skin surface of said portion forms an affixation with an injection overmolded second polymer, said first crosslinked profile having been crosslinked from a method selected from the group consisting of radiation and silane;

inserting at least a portion of said heated portion of said tube having an inner diameter while said heated portion is still in a heated condition, at least partially into a mold and at least partially onto a cylindrical mandrel, the mandrel having a base and a tip, an outer diameter of said mandrel dimensioned so as to allow the inner diameter of the tube to slide thereon, said mold containing a void for receiving a second polymer, the void co-acting with the mandrel and the tube to define an overmolding shape; and

injection molding a second polymer over the tube and the mandrel in the void of the mold forming said affixation with said first polymer, said affixation between said first and second polymers being able to pass a hot burst pressure test applicable to an intended end use for said combination of said overmolded polymer and crosslinked profile at 180° F. in which increasing test pressure within the first and second profiles causes a burst failure without any visible separation between said first and second profiles after said test.

10. The process of claim 9 which further comprises the step of

crosslinking said second polymer from an initial degree of crosslinking to a final degree of crosslinking, said step of crosslinking said second polymer using a crosslinking methodology selected from the group consisting of radiation and silane.

11. The process of claim 9 wherein

the first and second polymers are polyethylene.

12. The process of claim 11 wherein

a final degree of crosslinking of said second polymer is greater than 65%.

13. The process of claim 12 wherein

a final degree of crosslinking of said second polymer is greater than 70%.

14. The process of claim 9 wherein

said second polymer is at least partially crosslinked before the step of crosslinking.

15. The process of claim 11 wherein

said first and second polymers are crosslinked to approximately the same final degree.

16. A process for injection overmolding crosslinked tubes comprising the steps of:

heating at least a portion of a skin surface of a tube of a first polymer radiation crosslinked to at least 65% with a heating means to at least approximately 112° F. and less than approximately 269° F. so that said skin surface of said portion forms an affixation with an injection overmolded second polymer;

inserting at least a portion of said heated portion of said tube having an inner diameter while said heated portion is still in a heated condition, at least partially into a mold and at least partially onto a cylindrical mandrel, the mandrel having a base and a tip, an outer diameter of said mandrel dimensioned so as to allow the inner diameter of the tube to slide thereon, said mold containing a void for receiving a second polymer, the void co-acting with the mandrel and the tube to define an overmolding shape; and

injection molding a second polymer over the tube and the mandrel in the void of the mold forming said affixation with said first polymer, said affixation between said first and second polymers being able to pass a hot burst pressure test applicable to an intended end use for said combination of said overmolded polymer and crosslinked profile at 180° F. in which increasing test pressure within the first and second profiles causes a burst failure without any visible separation between said first and second profiles after said test.

17. The process of claim 16 which further comprises the step of

radiation crosslinking said second polymer from an initial degree of crosslinking to a final degree of crosslinking.

18. The process of claim 17 wherein

the first and second polymers are polyethylene.

19. The process of claim 18 wherein

a final degree of crosslinking of said second polymer is greater than 65%.

20. The process of claim 11 wherein

said first and second polymers are crosslinked to approximately the same final degree.