Two-step synthesis of manganese oxide nanostructures on carbon for supercapacitor applications
View Patent ↗A process to deposit a conformal coating of manganese oxide nanocrystals within a high surface area connected pore structure of a carbon paper electrode. A two-step process is utilized. In the first step the carbon paper electrode is immersed in an alkaline manganese oxide solution to form a nanocrystal seed layer on the surface and within the pores of the carbon paper. In the second step the seeded carbon paper is immersed in an acidic manganese oxide solution. The result is a densely packed continuous conformal nanocrystal coating both on the surface of the carbon and deep within its pores. The carbon paper is highly suitable for use as an electrode in a supercapacitor.
1. A process for forming a conformal nanoscale metal oxide coating on a porous carbon sample, comprising:
immersing the carbon sample in an alkaline metal oxide solution at a temperature of about 25° C. to about 400° C. for a time of about 1 minute to about 20 hours to form a seed layer of metal oxide nanocrystals on the carbon sample; and
immediately thereafter immersing the seeded carbon sample in an acidic metal oxide solution at a temperature of about 25° C. to about 400° C. for a time of about 5 minutes to about 20 hours;
wherein a densely packed thin conformal layer of metal oxide nanocrystals is formed on the surface and within the pores of the carbon sample.
2. The process according to claim 1 , wherein the metal oxide comprises manganese oxide (MnO 2 ).
3. The process according to claim 1 , wherein the metal oxide comprises one of lithium manganese oxide, ruthenium oxide, and zinc oxide.
4. The process according to claim 1 , wherein the carbon sample comprises a carbon paper electrode configured for use in a supercapacitor.
5. The process according to claim 1 , wherein the carbon sample comprises one of solid carbon, carbon nanotubes, carbon aerogel, graphitic carbon, and graphene.
6. The process according to claim 1 , wherein the carbon sample is immersed in the alkaline solution in an open container to form the seeded carbon sample.
7. The process according to claim 6 , wherein the seeded carbon sample is immersed in the acid solution in an open container.
8. The process according to claim 6 , wherein the seeded carbon sample is immersed in the acid solution in a pressure-restricted vessel.
9. The process according to claim 1 , wherein the carbon sample is immersed in the alkaline solution in a beaker for 30 minutes at about 90° C. to form the seeded carbon sample.
10. The process according to claim 1 , wherein the carbon sample is immersed in the alkaline solution in a pressure-restricted vessel to form the seeded carbon sample.
11. The process according to claim 10 , wherein the seeded carbon sample is immersed in the acid solution in an open container.
12. The process according to claim 10 , wherein the seeded carbon sample is immersed in the acid solution in a pressure-restricted vessel.
13. The process according to claim 1 , wherein the metal oxide coating is formed from a single metal oxide.