Monovinylarene conjugated diene copolymer compositions for acrylate blends
View Patent ↗The present invention relates to monovinylarene-conjugated diene copolymer compositions adapted for blendability with acrylate polymers. In some embodiments, such compositions are provided that are particularly resistant to blocking when stored in pellet form.
1. A composition comprising:
a monovinylarene-conjugated diene block copolymer;
wherein the block copolymer has two modes and three tapered blocks;
wherein the monovinylarene in the three tapered blocks comprises less than 25 wt % of the block copolymer;
wherein the block copolymer comprises at least a first and a second charge of monovinylarene, wherein the first charge has a weight ratio to the second charge in the range of 1:2 to 2:1;
wherein the block copolymer comprises from 30 to 40 wt % diene;
wherein a monoblock formed from a first charge of monovinylarene in the block copolymer preceding the three tapered blocks has a molecular weight in the range of 25,000 to 65,000 gram per mole; and
wherein the block copolymer is prepared by the addition of a first initiator charge and a second initiator charge, and wherein the first initiator charge contains less initiator than the second initiator charge.
2. The composition of claim 1 , wherein the block copolymer comprises at least 34 wt % diene.
3. The composition of claim 1 , wherein the block copolymer comprises from 36 to 38 wt % diene.
4. The composition of claim 1 , wherein the monovinylarene is styrene and the diene is butadiene.
5. The composition of claim 1 , wherein the monovinylarene in the three tapered blocks comprises less than 20 wt % of the block copolymer.
6. The composition of claim 1 , wherein the monovinylarene contains from 8 to 18 carbon atoms and the conjugated diene contains from 4 to 12 carbon atoms.
7. The composition of claim 1 , wherein the block copolymer is prepared by coupling the following polymer chains:
S1-S2-B1/S3-B2/S4-B3/S5-Li
S2-B1/S3-B2/S4-B3/S5-Li
wherein S represents monovinylarene blocks, B/S represents tapered blocks of conjugated diene/monovinylarene and Li is residue from a monoalkali metal initiator.
8. The composition of claim 1 , wherein the first initiator charge and the second initiator charge comprise n-butyl lithium.
9. The composition of claim 1 :
wherein the monovinylarene is styrene and the diene is butadiene;
wherein the monovinylarene in the three tapered blocks comprises less than 20 wt % of the block copolymer; and
wherein the block copolymer comprises at least 36 wt % diene.
10. A method of producing a monovinylarene-conjugated diene block copolymer suited for blending with monovinylarene acrylate copolymers, comprising:
sequentially contacting under polymerization conditions at least one monovinylarene monomer, an organomonoalkali metal initiator, at least one conjugated diene monomer, and thereafter coupling with a polyfunctional coupling agent to form the block copolymer;
wherein the block copolymer has two modes and three tapered blocks;
wherein the monovinylarene in the three tapered blocks comprises less than 25 wt % of the block copolymer;
wherein the block copolymer comprises at least a first and a second charge of monovinylarene, wherein the first charge has a weight ratio to the second charge in the range of 1:3 to 3:1;
wherein the block copolymer comprises at least from 30 to 40 wt % diene;
wherein a monoblock formed from a first charge of monovinylarene in the block copolymer preceding the three tapered blocks has a molecular weight in the range of 25,000 to 65,000 gram per mole; and
wherein the block copolymer is prepared by the addition of a first initiator charge and a second initiator charge, and wherein the first initiator charge contains less of the organomonoalkali metal initiator than the second initiator charge.
11. The method of claim 10 , wherein the first charge of monovinylarene has a weight ratio to the second charge of monovinylarene in the range of 1:2 to 2:1.
12. The method of claim 10 , wherein the block copolymer has a blocking force of less than 175 lb.
13. The method of claim 10 , wherein the block copolymer has a blocking force of less than 50 lb.
14. The method of claim 10 , wherein the monovinylarene is styrene and the diene is butadiene and wherein the block copolymer comprises from 36 to 38 wt % diene.
15. A composition comprising:
a monovinylarene-conjugated diene block copolymer;
wherein the block copolymer has two modes and three tapered blocks;
wherein the monovinylarene in the three tapered blocks comprises less than 25 wt % of the block copolymer;
wherein the block copolymer comprises at least 30 wt % diene; and
wherein the block copolymer is prepared by the addition of a first initiator charge and a second initiator charge, and wherein the first initiator charge contains less initiator than the second initiator charge.
16. The composition of claim 15 , wherein the block copolymer has a blocking force of less than 175 lb.
17. The composition of claim 15 , wherein the block copolymer has a blocking force of less than 50 lb.
18. The composition of claim 15 , wherein the monovinylarene in the three tapered blocks comprises less than 20 wt % of the block copolymer.
19. The composition of claim 15 , wherein the block copolymer comprises at least a first and a second charge of monovinylarene, and wherein the first charge has a weight ratio to the second charge in the range of 1:3 to 3:1.
20. The composition of claim 15 , wherein the block copolymer comprises at least a first and a second charge of monovinylarene, and wherein the first charge has a weight ratio to the second charge in the range of 1:2 to 2:1.
21. The composition of claim 15 , wherein the block copolymer comprises from 36 to 38 wt % diene.
22. The composition of claim 15 , wherein the block copolymer comprises at least 34 wt % diene.
23. A styrene polymer blend composition comprising:
an acrylate polymer, wherein the acrylate polymer is a blend or copolymer of methyl methacrylate and styrene; and
a monovinylarene-conjugated diene block copolymer;
wherein the block copolymer has two modes and three tapered blocks;
wherein the monovinylarene in the three tapered blocks comprises less than 25 wt % of the block copolymer;
wherein the block copolymer comprises at least a first and a second charge of monovinylarene, wherein the first charge has a weight ratio to the second charge in the range of 1:2 to 2:1;
wherein the block copolymer comprises from 30 to 40 wt % diene;
wherein a monoblock formed from a first charge of monovinylarene in the block copolymer preceding the three tapered blocks has a molecular weight in the range of 25,000 to 65,000 gram per mole; and
wherein the block copolymer is prepared by the addition of a first initiator charge and a second initiator charge, and wherein the first initiator charge contains less initiator than the second initiator charge.
24. The composition of claim 23 , wherein the block copolymer comprises from 36 to 38 wt % diene.
25. The composition of claim 23 , wherein the monovinylarene is styrene and the diene is butadiene, and wherein the block copolymer is prepared by coupling the following polymer chains:
S1-S2-B1/S3-B2/S4-B3/S5-Li
S2-B1/S3-B2/S4-B3/S5-Li
wherein S represents monovinylarene blocks, B/S represents tapered blocks of conjugated diene/monovinylarene and Li is residue from a monoalkali metal initiator.